Comparison of different experimental and analytical measures of the thermal annealing response of neutron-irradiated RPV steels
- Oak Ridge National Lab., TN (United States). Metals and Ceramics Div.
The thermal annealing response of several materials as indicated by Charpy transition temperature (TT) and upper-shelf energy (USE), crack initiation toughness, K{sub Jc}, predictive models, and automated-ball indentation (ABI) testing are compared. The materials investigated are representative reactor pressure vessel (RPV) steels (several welds and a plate) that were irradiated for other tasks of the Heavy-Section Steel Irradiation (HSSI) Program and are relatively well characterized in the unirradiated and irradiated conditions. They have been annealed at two temperatures, 343 and 454 C (650 and 850 F) for varying lengths of time. The correlation of the Charpy response and the fracture toughness, ABI, and the response predicted by the annealing model of Eason et al. for these conditions and materials appears to be reasonable. The USE after annealing at the temperature of 454 C appears to recover at a faster rate than the TT, and even over-recovers (i.e., the recovered USE exceeds that of the unirradiated material).
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC05-96OR22464
- OSTI ID:
- 679499
- Report Number(s):
- CONF-960643-; TRN: 99:009432
- Resource Relation:
- Conference: 18. symposium on effects of radiation on materials, Hyannis, MA (United States), 25-27 Jun 1996; Other Information: PBD: 1999; Related Information: Is Part Of Effects of radiation on materials: 18. international symposium; Nanstad, R.K. [ed.] [Oak Ridge National Lab., TN (United States)]; Hamilton, M.L.; Garner, F.A. [eds.] [Pacific Northwest National Lab., Richland, WA (United States)]; Kumar, A.S. [ed.] [Univ. of Missouri, Rolla, MO (United States)]; PB: 1261 p.; ASTM special technical publication 1325
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of annealing time on the recovery of Charpy V-notch properties of irradiated high-copper weld metal
Comparison of fracture toughness and Charpy impact properties recovery by thermal annealing of irradiated reactor pressure vessel steels