Influence of roll and solution treatment processing on shape memory effect of Fe-14Mn-5Si-9Cr-5Ni alloy
Journal Article
·
· Journal of Materials Engineering and Performance
- Xi`an Jiaotong Univ. (China). School of Material Science and Engineering
The shape memory effect was studied in an Fe-14Mn-5Si-9Cr-5Ni alloy rerolled at 1123 K after hot rolling at 1423 K, followed by solution treatment at different temperatures. It was found that the alloy exhibits a maximum degree of shape recovery in a bending test and a complete recovery tensile strain of 2.2% in samples that were solution heated at 973 K for 600 s and then quenched in water. The rerolled processing at 1123 K after hot rolling at 1423 K and the microstructure under solution treatment state are important for obtaining a good shape memory effect in the alloy.
- OSTI ID:
- 669811
- Journal Information:
- Journal of Materials Engineering and Performance, Journal Name: Journal of Materials Engineering and Performance Journal Issue: 5 Vol. 7; ISSN 1059-9495; ISSN JMEPEG
- Country of Publication:
- United States
- Language:
- English
Similar Records
Relationships between original microstructure and shape memory effect in an Fe-14Mn-5Si-9Cr-5Ni alloy
On the improvement of shape memory effect in Fe-16Mn-5Si-9Cr-4Ni alloys by thermomechanical treatment
The shape recovery conditions for Fe–Mn–Si alloys: An interplay between martensitic transformation and plasticity
Journal Article
·
Thu Oct 01 00:00:00 EDT 1998
· Materials Research Bulletin
·
OSTI ID:655378
On the improvement of shape memory effect in Fe-16Mn-5Si-9Cr-4Ni alloys by thermomechanical treatment
Journal Article
·
Wed Jun 15 00:00:00 EDT 1994
· Scripta Metallurgica et Materialia; (United States)
·
OSTI ID:7303392
The shape recovery conditions for Fe–Mn–Si alloys: An interplay between martensitic transformation and plasticity
Journal Article
·
Tue May 15 00:00:00 EDT 2018
· Materials Characterization
·
OSTI ID:22804990