Solder flow over fine line PWB surface finishes
The rapid advancement of interconnect technology has stimulated the development of alternative printed wiring board (PWB) surface finishes to enhance the solderability of standard copper and solder-coated surfaces. These new finishes are based on either metallic or organic chemistries. As part of an ongoing solderability study, Sandia National Laboratories has investigated the solder flow behavior of two azole-based organic solderability preservations, immersion Au, immersion Ag, electroless Pd, and electroless Pd/Ni on fine line copper features. The coated substrates were solder tested in the as-fabricated and environmentally-stressed conditions. Samples were processed through an inerted reflow machine. The azole-based coatings generally provided the most effective protection after aging. Thin Pd over Cu yielded the best wetting results of the metallic coatings, with complete dissolution of the Pd overcoat and wetting of the underlying Cu by the flowing solder. Limited wetting was measured on the thicker Pd and Pd over Ni finishes, which were not completely dissolved by the molten solder. The immersion Au and Ag finishes yielded the lowest wetted lengths, respectively. These general differences in solderability were directly attributed to the type of surface finish which the solder came in contact with. The effects of circuit geometry, surface finish, stressing, and solder processing conditions are discussed.
- Research Organization:
- Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 666160
- Report Number(s):
- SAND-98-0635C; CONF-981022-; ON: DE98007100; BR: DP0102023; TRN: AHC29819%%316
- Resource Relation:
- Conference: Institute for Interconnecting and Packaging Electronics Circuits/Surface Mount Technology Association electronics assembly expo, Providence, RI (United States), 27-29 Oct 1998; Other Information: PBD: [1998]
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of pre-stressing and flux on the flow of solder on PWB copper surfaces
Assessment of circuit board surface finishes for electronic assembly with lead-free solders