Stress-induced martensitic transformation of a NiTi alloy in isothermal shear, tension and compression
Journal Article
·
· Acta Materialia
- Inst. National Polytechnique, Grenoble (France)
The thermomechanical behavior of stress-induced martensitic transformation in an equiatomic NiTi alloy was investigated with respect to different deformation modes including uniaxial tension, compression and shear of plate specimens at different temperatures above the M{sub s} temperature. Results showed that loading conditions have significant influences on the deformation behavior of the alloy. In particular, deformation behavior was observed to be asymmetric in tension and in compression. The physical origins of such an asymmetry ar explored. Comparison among the results obtained from the tension, compression and shear tests disproves the use of classical Von Mises equivalent in the modelling of the three-dimensional behavior of martensitic transformation in this alloy. Based on this analysis, another criterion for yielding, which involves the third stress invariant, is therefore suggested.
- OSTI ID:
- 665208
- Journal Information:
- Acta Materialia, Journal Name: Acta Materialia Journal Issue: 15 Vol. 46; ISSN 1359-6454; ISSN ACMAFD
- Country of Publication:
- United States
- Language:
- English
Similar Records
Martensite transformation in NiTi alloys induced by tensile stress pulses
Asymmetry of stress-strain curves under tension and compression for NiTi shape memory alloys
Tension-compression asymmetry of the stress-strain response in aged single crystal and polycrystalline NiTi
Conference
·
Sat Dec 31 23:00:00 EST 1988
·
OSTI ID:5671981
Asymmetry of stress-strain curves under tension and compression for NiTi shape memory alloys
Journal Article
·
Fri Jul 24 00:00:00 EDT 1998
· Acta Materialia
·
OSTI ID:634671
Tension-compression asymmetry of the stress-strain response in aged single crystal and polycrystalline NiTi
Journal Article
·
Tue Mar 09 23:00:00 EST 1999
· Acta Materialia
·
OSTI ID:338425