Characterization of electron beam melted uranium - 6% niobium ingots
Conference
·
OSTI ID:646465
A study was undertaken at Lawrence Livermore National Laboratory to characterize uranium, 6{percent} niobium ingots produced via electron beam melting,hearth refining and continuous casting and to compare this material with conventional VIM/skull melt /VAR material. Samples of both the ingot and feed material were analyzed for niobium, trace metallic elements, carbon, oxygen and nitrogen. Ingot samples were also inspected metallographically and via microprobe analysis.
- Research Organization:
- Lawrence Livermore National Lab., CA (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 646465
- Report Number(s):
- UCRL-JC--128691; CONF-9710176--; ON: DE98052269; BR: DP0401042
- Country of Publication:
- United States
- Language:
- English
Similar Records
Characterization of U-6Nb ingots produced via the electron beam cold hearth refining process
Homogenization of arc-melted uranium-6 weight percent niobium alloy ingots
Alloying titanium and niobium via electron beam cold hearth melting
Conference
·
Thu Nov 13 23:00:00 EST 1997
·
OSTI ID:300435
Homogenization of arc-melted uranium-6 weight percent niobium alloy ingots
Technical Report
·
Mon Jan 30 23:00:00 EST 1978
·
OSTI ID:5154532
Alloying titanium and niobium via electron beam cold hearth melting
Technical Report
·
Fri Sep 27 00:00:00 EDT 2019
·
OSTI ID:1603870