Residual stresses in weld deposited clad pressure vessels and nozzles
- Westinghouse Electric Co., West Mifflin, PA (United States)
- Univ. of Tulsa, OK (United States)
Results of through-thickness residual stress measurements are provided for a variety of samples of weld deposited 308/309L stainless steel and Alloy 600 cladding on low-alloy pressure vessel ferritic steels. Clad thicknesses between 5 and 9mm on samples that vary in thickness from 45 to 200mm were studied. The samples were taken from flat plates, from a spherical head of a pressure vessel, from a ring-segment of a nozzle bore, and from the transition radius between a nozzle and a pressure vessel shell. A layer removal method was used to measure the residual stresses. The effects of uncertainties in elastic constants (Young`s modulus and Poisson`s ratio) as well as experimental error are assessed. All measurements were done at room temperature. The results of this work indicate that curvature plays a significant role in cladding residual stress and that tensile residual stresses as high as the yield stress can be measured in the cladding material. Since the vessel from which the spherical and nozzle corner samples were taken was hydrotested, and the flat plate specimens were taken from specimens used in mechanical fatigue testing, these results suggest that rather high tensile residual stresses can be retained in the cladding material even after some mechanical loading associated with hydrotesting and that higher levels of hydrotest loading would be required to alter the cladding residual stresses.
- Research Organization:
- Westinghouse Electric Corp., West Mifflin, PA (United States)
- Sponsoring Organization:
- USDOE Assistant Secretary for Nuclear Energy, Washington, DC (United States)
- DOE Contract Number:
- AC11-93PN38195
- OSTI ID:
- 645604
- Report Number(s):
- WAPD-T--3181; CONF-980708--; ON: DE98004959
- Country of Publication:
- United States
- Language:
- English
Similar Records
Experimental evaluation of residual stresses in a weld clad plate and clad test specimens
Fatigue crack growth testing of sub-clad defects