Processing and thermal stability of nano-Mg{sub 2}Si intermetallic compound
Journal Article
·
· Scripta Metallurgica et Materialia
- Academia Sinica, Hefei (China). Institute of Solid State Physics
Ball-milling of a crystalline elemental powder mixture (Mechanical Alloying, MA), or of a crystalline intermetallic compound (Mechanical Milling, MM), is of particular interest not only for forming alloys which are dispersion strengthened by a uniform distribution of fine, stable particles, but for creating nanometer-sized crystalline materials in which the solubility of some elements may be several orders of magnitude larger than in the case of single crystals. In this paper the processing and the thermal stability of the nanometer-sized Mg{sub 2}Si intermetallic compound prepared by both MA and MM techniques are reported and discussed.
- OSTI ID:
- 64369
- Journal Information:
- Scripta Metallurgica et Materialia, Vol. 32, Issue 9; Other Information: PBD: 1 May 1995
- Country of Publication:
- United States
- Language:
- English
Similar Records
The amorphization of intermetallic compounds by mechanical alloying/milling
Investigation of alloying effects in aluminum dispersion strengthened with Al$sub 2$O$sub 3$
Metastable phases in the Al sub 3 X (X = Ti, Zr, and Hf) intermetallic system
Miscellaneous
·
Tue Jan 01 00:00:00 EST 1991
·
OSTI ID:64369
Investigation of alloying effects in aluminum dispersion strengthened with Al$sub 2$O$sub 3$
Technical Report
·
Wed Oct 01 00:00:00 EDT 1975
·
OSTI ID:64369
Metastable phases in the Al sub 3 X (X = Ti, Zr, and Hf) intermetallic system
Journal Article
·
Fri Nov 01 00:00:00 EST 1991
· Scripta Metallurgica; (United States)
·
OSTI ID:64369