Interface structure of directionally solidified CoO-ZrO{sub 2}(Y{sub 2}O{sub 3}) eutectic
Conference
·
OSTI ID:62856
- Tohoku Univ., Sendai (Japan)
The interface structure of directionally solidified CoO-ZrO{sub 2}(Y{sub 2}O{sub 3}) eutectic was investigated by transmission electron microscopy. The interface of the lamella was found to have the orientation relationship of (001) cubic ZrO{sub 2} // (111) CoO and steps with periodic spacing. Precipitation of the Co{sub 3}O{sub 4} or Co phase was observed at the interface between cubic ZrO{sub 2} and CoO under experimental atmospheric conditions during directional solidification and successive cooling.
- OSTI ID:
- 62856
- Report Number(s):
- CONF-940315--
- Country of Publication:
- United States
- Language:
- English
Similar Records
Interlamellar residual stresses in single grains of NiO-ZrO{sub 2}(cubic) directionally solidified eutectics
Microanalysis of directionally solidified cobalt oxide-zirconia eutectic
Microanalysis of directionally solidified cobalt oxide-zirconia eutectic
Journal Article
·
Fri Oct 31 23:00:00 EST 1997
· Journal of the American Ceramic Society
·
OSTI ID:556423
Microanalysis of directionally solidified cobalt oxide-zirconia eutectic
Conference
·
Tue Jun 01 00:00:00 EDT 1993
·
OSTI ID:10157608
Microanalysis of directionally solidified cobalt oxide-zirconia eutectic
Conference
·
Thu Dec 31 23:00:00 EST 1992
·
OSTI ID:6399681