Fabrication of fiber-reinforced ceramic composites by chemical vapor infiltration
Technical Report
·
OSTI ID:6213764
Ceramic fiber-ceramic matrix composites are of interest because of their potentially higher strength and toughness. A vacuum forming technique was used to fabricate low-density structures from SiC fibers. These fibrous structures were then infiltrated by chemical vapor deposition. Matrices of Si/sub 3/N/sub 4/ and SiC have been deposited.
- Research Organization:
- Oak Ridge National Lab., TN (USA)
- DOE Contract Number:
- AC05-84OR21400
- OSTI ID:
- 6213764
- Report Number(s):
- ORNL/TM-9235; ON: DE85003809
- Country of Publication:
- United States
- Language:
- English
Similar Records
Fabrication of fiber reinforced ceramic composites by chemical vapor infiltration
Fiber-reinforced ceramic composites made by chemical vapor infiltration
Chemical vapor infiltration of fiber-reinforced ceramic composites
Conference
·
Sat Dec 31 23:00:00 EST 1983
·
OSTI ID:6105132
Fiber-reinforced ceramic composites made by chemical vapor infiltration
Technical Report
·
Mon Dec 31 23:00:00 EST 1984
·
OSTI ID:5385771
Chemical vapor infiltration of fiber-reinforced ceramic composites
Conference
·
Tue Dec 31 23:00:00 EST 1985
·
OSTI ID:6040755
Related Subjects
36 MATERIALS SCIENCE
360301* -- Composite Materials-- Preparation & Fabrication-- (-1987)
CARBIDES
CARBON COMPOUNDS
CERAMICS
CHEMICAL COATING
CHEMICAL VAPOR DEPOSITION
COMPOSITE MATERIALS
DEPOSITION
FABRICATION
FIBERS
MATERIALS
NITRIDES
NITROGEN COMPOUNDS
PNICTIDES
REINFORCED MATERIALS
SILICON CARBIDES
SILICON COMPOUNDS
SILICON NITRIDES
SURFACE COATING
360301* -- Composite Materials-- Preparation & Fabrication-- (-1987)
CARBIDES
CARBON COMPOUNDS
CERAMICS
CHEMICAL COATING
CHEMICAL VAPOR DEPOSITION
COMPOSITE MATERIALS
DEPOSITION
FABRICATION
FIBERS
MATERIALS
NITRIDES
NITROGEN COMPOUNDS
PNICTIDES
REINFORCED MATERIALS
SILICON CARBIDES
SILICON COMPOUNDS
SILICON NITRIDES
SURFACE COATING