Quantitative measurement of the development of recrystallization texture in OFE copper
Conference
·
OSTI ID:6201363
- Drexel Univ., Philadelphia, PA (USA). Dept. of Materials Engineering
- Los Alamos National Lab., NM (USA)
High purity OFE copper samples, cold rolled 58, 73 and 90%, were studied at different fractions recrystallized to follow the change of texture, the associated kinetics, release of stored energy, growth rates and microstructures. Higher strains led to a stronger copper deformation component and a stronger cube recrystallization component. The strength of the cube texture correlated strongly with the frequency of cube nuclei at the early stage of recrystallization for the 73 and 90% reductions. The kinetics had low Avrami exponents of 1.1, 1.2 and 1.8 respectively for the 3 rolling reductions. Average growth rates, G, decreased linearly with fraction recrystallized. However, unlike the study by Hutchinson et al., here the rate of stored energy release was constant with fraction recrystallized. 14 refs., 5 figs.
- Research Organization:
- Los Alamos National Lab., NM (USA)
- Sponsoring Organization:
- DOE/ER
- DOE Contract Number:
- W-7405-ENG-36
- OSTI ID:
- 6201363
- Report Number(s):
- LA-UR-90-3790; CONF-9009236--2; ON: DE91004834
- Country of Publication:
- United States
- Language:
- English
Similar Records
Cube texture generation dependence on deformation textures in cold rolled OFE copper
Development of recrystallization texture and microstructure in cold rolled copper
Recrystallization kinetics in copper: Comparison between techniques
Conference
·
Fri Oct 01 00:00:00 EDT 1993
·
OSTI ID:10188563
Development of recrystallization texture and microstructure in cold rolled copper
Conference
·
Mon Dec 30 23:00:00 EST 1996
·
OSTI ID:442170
Recrystallization kinetics in copper: Comparison between techniques
Journal Article
·
Sat Jul 01 00:00:00 EDT 1995
· Metallurgical Transactions, A
·
OSTI ID:87693