Test and Post-Test Analysis of a Thermacore, Inc. Nickel Powder Wick Heat Pipe Solar Reciever
Technical Report
·
OSTI ID:6190660
This report is a cradle-to-grave fabrication and postmortem analysis of a sodium-filled heat pipe solar receiver. The Stirling Thermal Motors Gen. H engine was tested with the Thermacore, Inc. heat pipe receiver on Sandia's Test Bed Concentrator II in the fall of 1996. Although engine performance was significantly increased relative to a direct insolation version of the receiver, hot spots did develop on the heat pipe receiver dome. Over the course of a couple of weeks, after tests were completed, the sodium was distilled out of this receiver, and the front dome was removed. Several failure spots and/or cracks (dubbed volcanoes ) were present on the surface of the wick. Postmortem analysis indicates that the cracks in the wick of the heat pipe are not a product of corrosive oxide action. Voids formed within the wick (created either by mechanical or thermal means) serve to concentrate phosphorous from the electroless plating into the liquid sodium. The presence of phosphorous has an apparently harmful effect on the wick. Examination of a virgin piece of the nickel wick material treated in the same manner as the bulk, prior to the introduction of sodium, would be the best baseline sample for comparison. This sample could be analyzed for phosphorous migration into the wick and determine if there is any initial crack formation from the sintering process. Utiortunately a sample of this material was not available during the preparation of this report. Continued work to determine the mechanism of crack formation could significantly increase the hours of available lifetime testing for future solar thermal heat pipe receivers
- Research Organization:
- Sandia National Laboratories (SNL), Albuquerque, NM, and Livermore, CA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 6190660
- Report Number(s):
- SAND99-1173; ON: DE00008377
- Country of Publication:
- United States
- Language:
- English
Similar Records
Test and Post-Test Analysis of a Thermacore, Inc. Nickel Powder Wick Heat Pipe Solar Reciever
Design, fabrication, and testing of a 30 kW{sub t} screen-wick heat- pipe solar receiver
Design, fabrication, and testing of a 30 kW sub t screen-wick heat- pipe solar receiver
Technical Report
·
Sat May 01 00:00:00 EDT 1999
·
OSTI ID:8377
Design, fabrication, and testing of a 30 kW{sub t} screen-wick heat- pipe solar receiver
Conference
·
Wed Jul 01 00:00:00 EDT 1992
·
OSTI ID:10158768
Design, fabrication, and testing of a 30 kW sub t screen-wick heat- pipe solar receiver
Conference
·
Tue Dec 31 23:00:00 EST 1991
·
OSTI ID:5068362