Improved silicon carbide for advanced heat engines. Annual report

Technical Report · Mon Sep 01 04:00:00 EDT 1986

OSTI ID:6163498

Whalen, T J; Winterbottom, W L

Work performed to develop silicon carbide materials of high strength and to form components of complex shape and high reliability is described. A beta-SiC powder and binder system was adapted to the injection molding process and procedures and process parameters developed capable of providing a sintered silicon carbide material with improved properties. The initial effort has been to characterize the baseline precursor materials (beta silicon carbide powder and boron and carbon sintering aids), develop mixing and injection molding procedures for fabricating test bars, and characterize the properties of the sintered materials. Parallel studies of various mixing, dewaxing, and sintering procedures have been carried out in order to distinguish process routes for improving material properties. A total of 276 MOR bars of the baseline material have been molded, and 122 bars have been fully processed to a sinter density of approximately 95 percent. The material has a mean MOR room temperature strength of 43.31 ksi (299 MPa), a Weibull characteristic strength of 45.8 ksi (315 MPa), and a Weibull modulus of 8.0. Mean values of the MOR strengths at 1000, 1200, and 14000 C are 41.4, 43.2, and 47.2 ksi, respectively. Strength controlling flaws in this material were found to consist of regions of high porosity and were attributed to agglomerates originating in the initial mixing procedures. The mean stress rupture lift at 1400 C of five samples tested at 172 MPa (25 ksi) stress was 62 hours and at 207 MPa (30 ksi) stress was 14 hours. New fluid mixing techniques have been developed which significantly reduce flaw size and improve the strength of the material. Initial MOR tests indicate the strength of the fluid-mixed material exceeds the baseline property by more than 33 percent.

• Research Organization: Ford Motor Co., Dearborn, MI (USA)
• OSTI ID: 6163498
• Report Number(s): N-89-15251; NASA-CR-179477; NAS-1.26:179477
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
360201* -- Ceramics
Cermets
& Refractories-- Preparation & Fabrication
ALLOYS
BORON ADDITIONS
BORON ALLOYS
CARBIDES
CARBON COMPOUNDS
DOCUMENT TYPES
FABRICATION
HIGH TEMPERATURE
MECHANICAL PROPERTIES
MOLDING
POWDERS
PROGRESS REPORT
SILICON CARBIDES
SILICON COMPOUNDS
SINTERING