Interrelationship of mechanical and corrosion-mechanical characteristics of type 12KhN4MF steel
Journal Article
·
· Sov. Mater. Sci. (Engl. Transl.); (United States)
Investigations presented include a comparative evaluation of the corrosionmechanical characteristics of specimens of high-strength chrome-nickelmolybdenum steel taking into consideration the different methods of melting of the original metal. A comparison of the corrosion-mechanical test results obtained with the results of acceptance tests are presented. A study of the fracture surfaces and the specimen material with the use of fractographic, macroscopic, and microscopic analyses is given. The systematization of the corrosion-mechanical test results with the use of methods of mathematical statistics are presented.
- Research Organization:
- G.V. Karpenko PhysicoMechanical Institute, Luov
- OSTI ID:
- 6115065
- Journal Information:
- Sov. Mater. Sci. (Engl. Transl.); (United States), Vol. 21:3; Other Information: Translated from Fiziko-Khimicheskaya Mekhanika Materialov, Vol. 21, No. 3, pp. 64-68, May-June, 1985
- Country of Publication:
- United States
- Language:
- English
Similar Records
Studies on the influence of metallurgical variables on the stress corrosion behavior of AISI 304 stainless steel in sodium chloride solution using the fracture mechanics approach
Effect of inclusions and microstructural characteristics on the mechanical properties and fracture behavior of a high-strength low-alloy steel
Influence of microstructure on stress corrosion cracking of mild steel in synthetic caustic-nitrate nuclear waste solution
Journal Article
·
Wed May 01 00:00:00 EDT 1996
· Metallurgical Transactions, A
·
OSTI ID:6115065
Effect of inclusions and microstructural characteristics on the mechanical properties and fracture behavior of a high-strength low-alloy steel
Journal Article
·
Fri Dec 01 00:00:00 EST 1995
· Journal of Materials Engineering and Performance
·
OSTI ID:6115065
Influence of microstructure on stress corrosion cracking of mild steel in synthetic caustic-nitrate nuclear waste solution
Thesis/Dissertation
·
Mon Dec 01 00:00:00 EST 1975
·
OSTI ID:6115065
Related Subjects
36 MATERIALS SCIENCE
CHROMIUM ALLOYS
CORROSION RESISTANCE
CRACK PROPAGATION
MECHANICAL TESTS
MOLYBDENUM ALLOYS
NICKEL ALLOYS
BRINELL HARDNESS
COMPARATIVE EVALUATIONS
CORROSION FATIGUE
CORROSIVE EFFECTS
DESTRUCTIVE TESTING
FRACTOGRAPHY
FRACTURE PROPERTIES
SODIUM CHLORIDES
STATISTICAL MODELS
STRESS CORROSION
TERNARY ALLOY SYSTEMS
YIELD STRENGTH
ALKALI METAL COMPOUNDS
ALLOY SYSTEMS
ALLOYS
CHEMICAL REACTIONS
CHLORIDES
CHLORINE COMPOUNDS
CORROSION
FATIGUE
HALIDES
HALOGEN COMPOUNDS
MATERIALS TESTING
MATHEMATICAL MODELS
MECHANICAL PROPERTIES
SODIUM COMPOUNDS
TESTING
360105* - Metals & Alloys- Corrosion & Erosion
360103 - Metals & Alloys- Mechanical Properties
CHROMIUM ALLOYS
CORROSION RESISTANCE
CRACK PROPAGATION
MECHANICAL TESTS
MOLYBDENUM ALLOYS
NICKEL ALLOYS
BRINELL HARDNESS
COMPARATIVE EVALUATIONS
CORROSION FATIGUE
CORROSIVE EFFECTS
DESTRUCTIVE TESTING
FRACTOGRAPHY
FRACTURE PROPERTIES
SODIUM CHLORIDES
STATISTICAL MODELS
STRESS CORROSION
TERNARY ALLOY SYSTEMS
YIELD STRENGTH
ALKALI METAL COMPOUNDS
ALLOY SYSTEMS
ALLOYS
CHEMICAL REACTIONS
CHLORIDES
CHLORINE COMPOUNDS
CORROSION
FATIGUE
HALIDES
HALOGEN COMPOUNDS
MATERIALS TESTING
MATHEMATICAL MODELS
MECHANICAL PROPERTIES
SODIUM COMPOUNDS
TESTING
360105* - Metals & Alloys- Corrosion & Erosion
360103 - Metals & Alloys- Mechanical Properties