Swelling of NiBe and copper alloys in FFTF
The swelling of tensile specimens irradiated in the MOTA-1B experiment at approx. 450/sup 0/C have been measured using immersion density. The majority of these specimens were constructed from various commercial copper alloys and exhibited density changes ranging from -0.66% to 16.6% swelling. The latter was obtained in a copper-0.1% silver sepecimen that reached 16 dpa, implying a swelling rate of at least 1%/dpa.
- Research Organization:
- Hanford Engineering Development Lab., Richland, WA (USA)
- DOE Contract Number:
- AC06-76FF02170
- OSTI ID:
- 6059381
- Report Number(s):
- HEDL-7496; ON: DE85007068
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of neutron irradiation at 450/sup 0/C and 16 dpa on the properties of various commercial copper alloys
Swelling of pure copper and copper alloys after high fluence irradiation in FFTF (Fast Flux Test Facility) at approximately 450/sup 0/C
Irradiation of copper alloys in FFTF
Conference
·
Mon Oct 01 00:00:00 EDT 1984
·
OSTI ID:6176475
Swelling of pure copper and copper alloys after high fluence irradiation in FFTF (Fast Flux Test Facility) at approximately 450/sup 0/C
Technical Report
·
Fri Feb 28 23:00:00 EST 1986
·
OSTI ID:6873722
Irradiation of copper alloys in FFTF
Technical Report
·
Wed May 23 00:00:00 EDT 1984
·
OSTI ID:7026126
Related Subjects
21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS
220600 -- Nuclear Reactor Technology-- Research
Test & Experimental Reactors
36 MATERIALS SCIENCE
360106* -- Metals & Alloys-- Radiation Effects
ALLOYS
BARYONS
BERYLLIUM ALLOYS
COPPER
COPPER ALLOYS
COPPER BASE ALLOYS
ELEMENTARY PARTICLES
ELEMENTS
EPITHERMAL REACTORS
FAST NEUTRONS
FAST REACTORS
FERMIONS
FFTF REACTOR
HADRONS
HIGH TEMPERATURE
IRRADIATION
LIQUID METAL COOLED REACTORS
METALS
NEUTRONS
NICKEL ALLOYS
NICKEL BASE ALLOYS
NUCLEONS
PHYSICAL RADIATION EFFECTS
RADIATION EFFECTS
REACTORS
RESEARCH AND TEST REACTORS
RESEARCH REACTORS
SILVER ADDITIONS
SILVER ALLOYS
SODIUM COOLED REACTORS
SWELLING
TEST REACTORS
TRANSITION ELEMENTS
220600 -- Nuclear Reactor Technology-- Research
Test & Experimental Reactors
36 MATERIALS SCIENCE
360106* -- Metals & Alloys-- Radiation Effects
ALLOYS
BARYONS
BERYLLIUM ALLOYS
COPPER
COPPER ALLOYS
COPPER BASE ALLOYS
ELEMENTARY PARTICLES
ELEMENTS
EPITHERMAL REACTORS
FAST NEUTRONS
FAST REACTORS
FERMIONS
FFTF REACTOR
HADRONS
HIGH TEMPERATURE
IRRADIATION
LIQUID METAL COOLED REACTORS
METALS
NEUTRONS
NICKEL ALLOYS
NICKEL BASE ALLOYS
NUCLEONS
PHYSICAL RADIATION EFFECTS
RADIATION EFFECTS
REACTORS
RESEARCH AND TEST REACTORS
RESEARCH REACTORS
SILVER ADDITIONS
SILVER ALLOYS
SODIUM COOLED REACTORS
SWELLING
TEST REACTORS
TRANSITION ELEMENTS