Microstructure of high-strain, high-strain-rate deformed tantalum

Journal Article · · Acta Materialia
; ;  [1]
  1. Univ. of California, San Diego, La Jolla, CA (United States)

Hat-shaped specimens of polycrystalline tantalum are subjected to high plastic shear strains ({gamma} = 170--910%) at strain rates exceeding 5 {times} 10{sup 4}/s in a compression split Hopkinson bar. The dynamic shear tests are performed at room and 600 K initial temperatures, under adiabatic and quasi-isothermal conditions, using UCSD`s recovery Hopkinson technique. The microstructure of the post-test specimens is examined with transmission electron microscopy (TEM). The plastic deformation is highly concentrated, producing a narrow shear-localization region of approximately 200 {micro}m in width. Slip of perfect screw dislocations, on the {l_brace}110{r_brace} primary planes along the <111> directions, is found to be the dominant deformation mechanism. Dynamic recovery takes place in the shear-localization regions of all adiabatically tested specimens, and evidence of dynamic recrystallization is observed in the specimen deformed to a shear strain of 910% at a 600 K initial temperature. The substrates of the adiabatically tested specimens include well-defined dislocation arrays, grouped dislocations, elongated dislocation cells, subgrains, and recrystallized micron-sized grains. The microstructure of isothermally tested specimens, on the other hand, features high dislocation density and inhomogeneous dislocation distribution. In light of the TEM observations, the relation between the microstructure and shear stress, the causes of strain inhomogeneity, the estimates adiabatic temperature within the shear-localization zone, the rapid quenching of the shearband at the end of the dynamic testing, the slip characteristics of dislocations in tantalum, and the formation mechanisms of dislocation loops, are discussed.

OSTI ID:
605853
Journal Information:
Acta Materialia, Journal Name: Acta Materialia Journal Issue: 4 Vol. 46; ISSN 1359-6454; ISSN ACMAFD
Country of Publication:
United States
Language:
English

Similar Records

High-strain, high-strain-rate behavior of tantalum
Journal Article · Sun Oct 01 00:00:00 EDT 1995 · Metallurgical Transactions, A · OSTI ID:131430

Structural evolution of materials in thick-walled cylinder test
Conference · Sat Dec 30 23:00:00 EST 1995 · OSTI ID:175197

Microstructure characterization of 316L deformed at high strain rates using EBSD
Journal Article · Wed Dec 14 23:00:00 EST 2016 · Materials Characterization · OSTI ID:22689662