Single-layer TiO/sub 2/ and multilayer TiO/sub 2/--SiO/sub 2/ optical coatings prepared from colloidal suspensions
Journal Article
·
· Appl. Opt.; (United States)
Single-layer coatings on fused silica substrates have been prepared from aqueous colloidal suspensions of titania at room temperature. These coatings were porous and had a refractive index of 1.9. Multilayer high reflectivity dielectric coatings were also prepared by laying down quarterwave thick alternating coats at room temperature of this titania with silica, prepared from a colloidal suspension of silica. Single-shot laser damage threshold measurements at 1064-nm wavelength with a pulse length of 1 ns were carried out for both the titania and titania--silica systems. These averaged 7.5 and 6.2 J/cm/sup 2/, respectively.
- Research Organization:
- Lawrence Livermore National Laboratory, P.O. Box 808, Livermore, California 94550
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 5923711
- Journal Information:
- Appl. Opt.; (United States), Journal Name: Appl. Opt.; (United States) Vol. 26:21; ISSN APOPA
- Country of Publication:
- United States
- Language:
- English
Similar Records
Single layer Al sub 2 O sub 3 ter dot H sub 2 O and multilayer Al sub 2 O sub 3 ter dot H sub 2 O--SiO sub 2 optical coatings prepared from colloidal suspensions
Preparation of dielectrics HR mirrors from colloidal oxide suspensions containing organic polymer binders
Preparation, characterization, and infrared emissivity property of optically active polyurethane/TiO{sub 2}/SiO{sub 2} multilayered microspheres
Journal Article
·
Fri Sep 15 00:00:00 EDT 1989
· Applied Optics; (USA)
·
OSTI ID:5650009
Preparation of dielectrics HR mirrors from colloidal oxide suspensions containing organic polymer binders
Conference
·
Tue Jul 19 00:00:00 EDT 1994
·
OSTI ID:369647
Preparation, characterization, and infrared emissivity property of optically active polyurethane/TiO{sub 2}/SiO{sub 2} multilayered microspheres
Journal Article
·
Sat Oct 15 00:00:00 EDT 2011
· Journal of Solid State Chemistry
·
OSTI ID:21580012
Related Subjects
36 MATERIALS SCIENCE
360201* -- Ceramics
Cermets
& Refractories-- Preparation & Fabrication
360204 -- Ceramics
Cermets
& Refractories-- Physical Properties
ANTIREFLECTION COATINGS
CHALCOGENIDES
COATINGS
DEPOSITION
DISPERSIONS
FABRICATION
LASERS
LAWRENCE LIVERMORE LABORATORY
NATIONAL ORGANIZATIONS
OPTICAL PROPERTIES
OXIDES
OXYGEN COMPOUNDS
PHYSICAL PROPERTIES
POROSITY
REFLECTIVE COATINGS
REFRACTIVITY
SUSPENSIONS
TITANIUM COMPOUNDS
TITANIUM OXIDES
TRANSITION ELEMENT COMPOUNDS
US AEC
US DOE
US ERDA
US ORGANIZATIONS
360201* -- Ceramics
Cermets
& Refractories-- Preparation & Fabrication
360204 -- Ceramics
Cermets
& Refractories-- Physical Properties
ANTIREFLECTION COATINGS
CHALCOGENIDES
COATINGS
DEPOSITION
DISPERSIONS
FABRICATION
LASERS
LAWRENCE LIVERMORE LABORATORY
NATIONAL ORGANIZATIONS
OPTICAL PROPERTIES
OXIDES
OXYGEN COMPOUNDS
PHYSICAL PROPERTIES
POROSITY
REFLECTIVE COATINGS
REFRACTIVITY
SUSPENSIONS
TITANIUM COMPOUNDS
TITANIUM OXIDES
TRANSITION ELEMENT COMPOUNDS
US AEC
US DOE
US ERDA
US ORGANIZATIONS