Anomalous behavior of cyclic deformation and fatigue properties of TiAl PST crystals under constant applied stress
- Osaka Univ., Suita, Osaka (Japan). Dept. of Materials Science and Engineering
Cyclic deformation and fatigue properties of TiAl PST crystals were investigated at room temperature under constant applied stress by focusing on the effect of {gamma} domains. Strong anisotropy in plastic behavior was observed depending on the angle ({phi}) between the loading axis and the lamellar planes. At {phi} = 0{degree} the {gamma} domains were divided into two groups of T-type and V-type depending on deformation substructure. In T-type and V-type domains, deformation twins and vein-like structure were mainly formed, respectively. Plastic strain energy for each cycle increased with increasing applied stress amplitude ({Delta}{sigma}) but an anomalous drop in the energy was found around {Delta}{sigma} = 440 MPa at {phi} = 0{degree}. The anomalous dependence of the plastic strain energy on {Delta}{sigma} was closely related to the deformation mode in the V-type domains. Deformation twins which were induced in the V-type domains in an early stage interrupted the to-and-fro motion of ordinary dislocations resulting in a rapid cyclic hardening. At {phi} = 45{degree}, shear deformation occurred along the lamellar planes, and ordinary dislocations and twins easily passed through the domain boundaries. The plastic strain energy monotonically increased as {Delta}{sigma} rose.
- OSTI ID:
- 590032
- Journal Information:
- Acta Materialia, Journal Name: Acta Materialia Journal Issue: 11 Vol. 45; ISSN 1359-6454; ISSN ACMAFD
- Country of Publication:
- United States
- Language:
- English
Similar Records
Deformation of polysynthetically twinned (PST) TiAl crystals at high strain rate and high temperature
Plastic deformation of V- and Zr-alloyed PST TiAl in tension and compression at room temperature