Numerical simulation of damage and progressive failures in composite laminates using the layerwise plate theory
The failure behavior of composite laminates is modeled numerically using the Generalized Layerwise Plate Theory (GLPT) of Reddy and a progressive failure algorithm. The Layerwise Theory of Reddy assumes a piecewise continuous displacement field through the thickness of the laminate and therefore has the ability to capture the interlaminar stress fields near the free edges and cut outs more accurately. The progressive failure algorithm is based on the assumption that the material behaves like a stable progressively fracturing solid. A three-dimensional stiffness reduction scheme is developed and implemented to study progressive failures in composite laminates. The effect of various parameters such as out-of-plane material properties, boundary conditions, and stiffness reduction methods on the failure stresses and strains of a quasi-isotropic composite laminate with free edges subjected to tensile loading is studied. The ultimate stresses and strains predicted by the Generalized Layerwise Plate Theory (GLPT) and the more widely used First Order Shear Deformation Theory (FSDT) are compared with experimental results. The predictions of the GLPT are found to be in good agreement with the experimental results both qualitatively and quantitatively, while the predictions of FSDT are found to be different from experimental results both qualitatively and quantitatively. The predictive ability of various phenomenological failure criteria is evaluated with reference to the experimental results available in the literature. The effect of geometry of the test specimen and the displacement boundary conditions at the grips on the ultimate stresses and strains of a composite laminate under compressive loading is studied. The ultimate stresses and strains are found to be quite sensitive to the geometry of the test specimen and the displacement boundary conditions at the grips. The degree of sensitivity is observed to depend strongly on the lamination sequence.
- Research Organization:
- Virginia Polytechnic Inst. and State Univ., Blacksburg, VA (United States)
- OSTI ID:
- 5840766
- Resource Relation:
- Other Information: Thesis (Ph.D.)
- Country of Publication:
- United States
- Language:
- English
Similar Records
Interlaminar stress recovery near free edge using a layerwise element with enhanced strains
Failure analysis of quasi-isotropic composite laminates with free edges under off-axis loading