Alternative acceptance criteria of girth weld defects in cross country pipelines. Final report
- Universiteit Gent (Belgium). Laboratory Soete
The failure behaviour of defective girth welds in large diameter pipe lines was assessed using radiographic and mechanised ultrasonic inspection, small scale (tensile, hardness, Charpy and CTOD) and wide plate tests. The specimens were taken from girth welds in API 5LX70 pipe of 1219 mm (48 inches) in diameter by 8,0 mm (0,323 inch) and 13,3 mm (0,524 inch) wall. The test welds were made with the SMAW (8 welds) and GMAW (9 welds) welding processes. Upon completion of the non-destructive tests, 96 curved wide plate specimens were tested to destruction under tensile load. Testing was performed at low temperature (-50{degrees}C/-58{degrees}F). Defect type, defect position and size were determined from photographs of the fracture face and macro sections (defect characterisation and sizing). In total, 290 typical surface breaking and embedded defects in SMAW or GMAW girth welds have been evaluated. The vast majority of these defects were grossly out of tolerance with respect to current weld quality (workmanship) acceptance levels. To allow the defect tolerance to be determined, the failure strains and stresses were correlated with a defect length determined for an equivalent 3 mm (0, 118 inch) deep defect. This target depth was chosen to represent the average height of one weld pass. The results of this approach have been compared to wall thickness, current workmanship and the EPRG Tier 2 defect limit for planar defects. The defect lengths were derived for rectangular, parabolic and elliptical defect representations.
- Research Organization:
- American Gas Association, Inc., Arlington, VA (United States). Pipeline Research Committee
- Sponsoring Organization:
- American Gas Association, Inc., Arlington, VA (United States)
- OSTI ID:
- 576124
- Report Number(s):
- AGA-98002887; CNN: Contract PR 202-9328; TRN: 98:001465
- Resource Relation:
- Other Information: PBD: Jun 1997
- Country of Publication:
- United States
- Language:
- English
Similar Records
Fracture behaviour of large diameter pipeline girth welds: Effect of weld metal yield strength. Part 1, final report
The effect of weld metal matching on girth weld performance. Volume 2, Experimental investigation: Final report