Results of crack-arrest tests on irradiated a 508 class 3 steel
Ten crack-arrest toughness values for irradiated specimens of A 508 class 3 forging steel have been obtained. The tests were performed according to the American Society for Testing and Materials (ASTM) Standard Test Method for Determining Plane-Strain Crack-Arrest Fracture Toughness, K{sub la} of Ferritic Steels, E 1221-88. None of these values are strictly valid in all five ASTM E 1221-88 validity criteria. However, they are useful when compared to unirradiated crack-arrest specimen toughness values since they show the small (averaging approximately 10{degrees}C) shifts in the mean and lower-bound crack-arrest toughness curves. This confirms that a low copper content in ASTM A 508 class 3 forging material can be expected to result in small shifts of the transition toughness curve. The shifts due to neutron irradiation of the lower bound and mean toughness curves are approximately the same as the Charpy V-notch (CVN) 41-J temperature shift. The nine crack-arrest specimens were irradiated at temperatures varying from 243 to 280{degrees}C, and to a fluence varying from 1.7 to 2.7 x 10{sup 19} neutrons/cm{sup 2} (> 1 MeV). The test results were normalized to reference values that correspond to those of CVN specimens irradiated at 284{degrees}C to a fluence of 3.2 x 10{sup 19} neutrons/cm{sup 2} (> 1 MeV) in the same capsule as the crack-arrest specimens. This adjustment resulted in a shift to lower temperatures of all the data, and in particular moved two data points that appeared to lie close to or lower than the American Society of Mechanical Engineers K{sub la} curve to positions that seemed more reasonable with respect to the remaining data. A special fixture was designed, fabricated, and successfully used in the testing. For reasons explained in the text, special blocks to receive the Oak Ridge National Laboratory clip gage were designed, and greater-than-standard crack-mouth opening displacements measured were accounted for. 24 refs., 13 figs., 12 tabs.
- Research Organization:
- Nuclear Regulatory Commission, Washington, DC (United States). Div. of Engineering Technology; Oak Ridge National Lab., TN (United States)
- Sponsoring Organization:
- Nuclear Regulatory Commission, Washington, DC (United States)
- DOE Contract Number:
- AC05-96OR22464
- OSTI ID:
- 576023
- Report Number(s):
- NUREG/CR--6447; ORNL--6894; ON: TI98004086
- Country of Publication:
- United States
- Language:
- English
Similar Records
Crack-arrest tests on two irradiated high-copper welds. Phase 2: Results of duplex-type experiments
Fracture toughness shifts in high-copper weldments (series 5 and 6)
Results of crack-arrest tests on two irradiated high-copper welds
Technical Report
·
Mon Feb 28 23:00:00 EST 1994
·
OSTI ID:10131847
Fracture toughness shifts in high-copper weldments (series 5 and 6)
Technical Report
·
Sun Oct 01 00:00:00 EDT 1995
·
OSTI ID:223650
Results of crack-arrest tests on two irradiated high-copper welds
Technical Report
·
Fri Nov 30 23:00:00 EST 1990
·
OSTI ID:6152342