Apparent thermal conductivity measurements by an unguarded technique
An unguarded longitudinal heat-flow apparatus for measuring the apparent thermal conductivity (lambda/sub a) of insulations was tested with mean specimen temperatures from 300 to 330/sup 0/K on samples up to 0.91 m wide, 1.52 m long, and 0.15 m thick. Heat flow is provided by a horizontal electrically heated Nichrome screen sandwiched between test samples that are bounded by temperature controlled copper plates and 9 cm of mineral fiber insulation. A determinate error analysis shows lambda/sub a/ measurement uncertainty to be less than +- 1.7% for insulating materials as thin as 3 cm. Three-dimensional thermal modeling indicates negligible error in lambda/sub a/ due to edge loss for insulations up to 7.62 cm thick when the temperature difference across the sample is measured at the sceen center. System repeatability and reproducibility were determined to be +- 0.2%. Differences of lambda/sub a/ results from the screen tester and results from the National Bureau of Standards were 0.1% for a 10-kg/m/sup 3/ Calibration Transfer Standard and 0.9% for 127-kg/m/sup 3/ fibrous glass board (SRM 1450b). Measurements on fiberglass and rock wool batt insulations showed the dependence of lambda/sub a/ on density, temperature, temperature difference, plate emittance, and heat flow direction. Results obtained for lambda/sub a/ as a function of density at 24/sup 0/C differed by less than 2% from values obtained with a guarded hot plate. These results demonstrate that this simple technique has the accuracy and sensitivity needed for useful lambda/sub a/ measurements on thermal insulating materials.
- Research Organization:
- Oak Ridge National Lab., TN (USA)
- DOE Contract Number:
- W-7405-ENG-26
- OSTI ID:
- 5727072
- Report Number(s):
- CONF-8310163-4; ON: DE84001964
- Resource Relation:
- Conference: 18. international thermal conductivity conference, Rapid City, SD, USA, 3 Oct 1983
- Country of Publication:
- United States
- Language:
- English
Similar Records
Steady-state and transient results on insulation materials
Technique for measuring the apparent thermal conductivity of flat insulations