Wetting of molybdenum by commercial brazing filler alloys
Conference
·
OSTI ID:5702033
Wettability tests have been conducted for each candidate filler alloy at several temperatures. A wetting index, which is a function of contact angle and braze alloy contact area, was determined for each filler alloy at each brazing temperature. The nature and extent of interaction between the brazing alloys and the molybdenum was also investigated. The microstructures of the braze alloys and the base metal were examined with optical metallography, scanning-electron microscopy, and electron microprobe techniques. Results of the present study are compared with results of a previous wettability study on type 304 stainless steel.
- Research Organization:
- Rockwell International Corp., Golden, CO (USA). Rocky Flats Plant
- DOE Contract Number:
- AC04-76DP03533
- OSTI ID:
- 5702033
- Report Number(s):
- RFP-3973; CONF-860594-3; ON: DE86010811
- Country of Publication:
- United States
- Language:
- English
Similar Records
Wettability of brazing alloys on molybdenum and TZM (Mo-Ti-Zr alloy)
Auger electron spectroscopy applied to braze wettability
Wetting and Brazing of Chromium Film-Deposited Alumina Using AgCu Filler Metal
Conference
·
Thu Dec 31 23:00:00 EST 1987
·
OSTI ID:5002085
Auger electron spectroscopy applied to braze wettability
Conference
·
Wed Dec 31 23:00:00 EST 1980
·
OSTI ID:6504882
Wetting and Brazing of Chromium Film-Deposited Alumina Using AgCu Filler Metal
Journal Article
·
Mon Oct 15 00:00:00 EDT 2018
· Journal of Materials Engineering and Performance
·
OSTI ID:22863272