Comparison of damage microstructures in neutron-irradiated vanadium and iron

Conference ·
OSTI ID:5696317
;
The cavity morphology and dislocation loop geometry in bcc vanadium are compared with the previously reported observations for neutron-irradiated iron. The specimens were vanadium (V) with 100 wppM of interstitial impurities and vanadium with boron carbide additions (V-B/sub 4/C) which were irradiated to approx. 1 dpa in the same Oak Ridge Research Reactor capsules as the iron specimens.
Research Organization:
Oak Ridge National Lab., TN (USA)
DOE Contract Number:
W-7405-ENG-26
OSTI ID:
5696317
Report Number(s):
CONF-830871-6; ON: DE83017189
Country of Publication:
United States
Language:
English

Similar Records

Comparison of damage microstructures in neutron-irradiated vanadium and iron
Journal Article · Fri Dec 31 23:00:00 EST 1982 · Proc. - Annu. Meet., Electron Microsc. Soc. Am.; (United States) · OSTI ID:6121776
Temperature dependence of the damage microstructures in neutron-irradiated vanadium
Technical Report · Fri Dec 31 23:00:00 EST 1982 · OSTI ID:5369662
Transmission electron microscope study of fusion-environment radiation damage in iron and iron-chromium alloys
Technical Report · Thu Jul 01 00:00:00 EDT 1982 · OSTI ID:5152825

Related Subjects

36 MATERIALS SCIENCE
360106* -- Metals & Alloys-- Radiation Effects
BORON CARBIDES
BORON COMPOUNDS
CARBIDES
CARBON COMPOUNDS
CAVITIES
COMPARATIVE EVALUATIONS
CRYSTAL DEFECTS
CRYSTAL STRUCTURE
DISLOCATIONS
ELEMENTS
HIGH TEMPERATURE
LINE DEFECTS
METALS
MICROSTRUCTURE
PHYSICAL RADIATION EFFECTS
RADIATION EFFECTS
TRANSITION ELEMENTS
VANADIUM