Synthesis and devolatilization of M-97 NVB silicone gum compounded into silica reinforced silicone base
Technical Report
·
OSTI ID:5632031
Silica reinforced silicon bases having 0.31 weight percent vinyl content were prepared by using a blend of low and high vinyl content devolatilized M-97 NVB silicone gum. The M-97 NVB is a custom dimethyl-, diphenyl-, methylvinylsiloxane gum. The silicon gum was devolatilized to evaluate the anticipated improved handling characteristics. Previous procured batches of M-97 NVB had not been devolatilized and difficult handling problems were encountered. The synthesis, devolatilization, and compound processes for the M-97 NVB silicone gum are discussed.
- Research Organization:
- Allied Corp., Kansas City, MO (USA). Bendix Kansas City Div.
- DOE Contract Number:
- AC04-76DP00613
- OSTI ID:
- 5632031
- Report Number(s):
- BDX-613-3533; ON: DE86013159
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of vinyl and phenyl contents of silicone gum on the properties of the elastomers and cellular silicone cushions
Evaluation of the use of processing aids in silicone elastomers and cellular silicones
Property of cellular silicone from high-vinyl silicone gums as a function of porosity (referenced to SE54 gum). [Density, porosity, deflection, compression set]
Technical Report
·
Mon Dec 01 23:00:00 EST 1980
·
OSTI ID:6830698
Evaluation of the use of processing aids in silicone elastomers and cellular silicones
Technical Report
·
Sun May 23 00:00:00 EDT 1982
·
OSTI ID:6540195
Property of cellular silicone from high-vinyl silicone gums as a function of porosity (referenced to SE54 gum). [Density, porosity, deflection, compression set]
Technical Report
·
Fri Aug 20 00:00:00 EDT 1982
·
OSTI ID:6202142