Magnetic and thermodynamic properties of nonsuperconducting (Y,Pr)Ba sub 2 Cu sub 3 O sub 6
- Center for Materials Research, Temple University, Philadelphia, Pennsylvania 19122 (USA)
- MARTECH, Florida State University, Tallahassee, Florida 32306 (USA)
The concentration dependence of the room-temperature lattice constants and the concentration and temperature dependence of the specific heat {ital C}({ital T}) and the magnetic susceptibility have been measured on the tetragonal, nonsuperconducting phase of Y{sub 1{minus}{ital x}}Pr{sub {ital x}}Ba{sub 2}Cu{sub 3}O{sub 6}. The effective paramagnetic moment {mu}{sub eff} is independent of {ital x} and has an average value of 2.7{plus minus}0.2 {mu}{sub {ital B}}. For PrBa{sub 2}Cu{sub 3}O{sub 6}, the Neel temperature {ital T}{sub {ital N}} for Pr moment ordering is 10.5 K as compared to {ital T}{sub {ital N}}=17 K for the orthorhombic PrBa{sub 2}Cu{sub 3}O{sub 7} phase. The {ital T}{sub {ital N}} is depressed rapidly with Y doping in the oxygen-depleted compound and goes to zero at {ital x}{approx}0.4--0.5. At low temperatures and {ital x}{le}0.5, {ital C}({ital T})/{ital T} vs {ital T}{sup 2} is nonlinear and shows a rapid decrease of {ital C}({ital T})/{ital T} indicative of strong magnetic correlations.
- OSTI ID:
- 5623272
- Journal Information:
- Journal of Applied Physics; (USA), Vol. 69:8; ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Superconductivity and magnetism in the system Y{sub 1{minus}x}Pr{sub x}Ba{sub 1.5}Sr{sub 0.5}Cu{sub 3}O{sub 7{minus}{delta}} (0{le}x{le}1.0)
Magnetic ordering in (Y sub 1 minus x Pr sub x )Ba sub 2 Cu sub 3 O sub 7 as observed by muon-spin relaxation
Related Subjects
BARIUM OXIDES
MAGNETIC SUSCEPTIBILITY
SPECIFIC HEAT
COPPER OXIDES
PRASEODYMIUM OXIDES
YTTRIUM OXIDES
HIGH-TC SUPERCONDUCTORS
LOW TEMPERATURE
MEDIUM TEMPERATURE
NEEL TEMPERATURE
QUANTITY RATIO
TEMPERATURE DEPENDENCE
TETRAGONAL LATTICES
ULTRALOW TEMPERATURE
VERY LOW TEMPERATURE
ALKALINE EARTH METAL COMPOUNDS
BARIUM COMPOUNDS
CHALCOGENIDES
COPPER COMPOUNDS
CRYSTAL LATTICES
CRYSTAL STRUCTURE
MAGNETIC PROPERTIES
OXIDES
OXYGEN COMPOUNDS
PHYSICAL PROPERTIES
PRASEODYMIUM COMPOUNDS
RARE EARTH COMPOUNDS
SUPERCONDUCTORS
THERMODYNAMIC PROPERTIES
TRANSITION ELEMENT COMPOUNDS
TRANSITION TEMPERATURE
YTTRIUM COMPOUNDS
360204* - Ceramics
Cermets
& Refractories- Physical Properties