Defects, fracture and fatigue
Book
·
OSTI ID:5620997
Among the areas considered are: dislocations, persistent-slip-bands, void creation, microcracking, micro-structure effects, micro/macro fracture mechanics, ductile fracture criteria, fatigue crack initiation and propagation, stress and failure analysis, deterministic and statistical crack models, and fracture control.
- OSTI ID:
- 5620997
- Country of Publication:
- United States
- Language:
- English
Similar Records
Mechanisms of intergranular fracture
Microstructural characteristics and cracking behavior during fatigue in austenitic stainless steel
Fatigue behavior of ADI: Some specific features
Book
·
Sun Aug 01 00:00:00 EDT 1999
·
OSTI ID:364079
Microstructural characteristics and cracking behavior during fatigue in austenitic stainless steel
Book
·
Tue Aug 01 00:00:00 EDT 1995
·
OSTI ID:86155
Fatigue behavior of ADI: Some specific features
Book
·
Tue Dec 30 23:00:00 EST 1997
·
OSTI ID:293099
Related Subjects
36 MATERIALS SCIENCE
360103* -- Metals & Alloys-- Mechanical Properties
360203 -- Ceramics
Cermets
& Refractories-- Mechanical Properties
360603 -- Materials-- Properties
CONTROL
CRYSTAL DEFECTS
CRYSTAL STRUCTURE
DEFECTS
DISLOCATIONS
DOCUMENT TYPES
FAILURE MODE ANALYSIS
FAILURES
FATIGUE
FRACTURE MECHANICS
FRACTURE PROPERTIES
FRACTURES
LINE DEFECTS
MATHEMATICAL MODELS
MATHEMATICS
MECHANICAL PROPERTIES
MECHANICS
MEETINGS
MICROSTRUCTURE
REVIEWS
SLIP
STATISTICS
STRESS ANALYSIS
SYSTEM FAILURE ANALYSIS
SYSTEMS ANALYSIS
VOIDS
360103* -- Metals & Alloys-- Mechanical Properties
360203 -- Ceramics
Cermets
& Refractories-- Mechanical Properties
360603 -- Materials-- Properties
CONTROL
CRYSTAL DEFECTS
CRYSTAL STRUCTURE
DEFECTS
DISLOCATIONS
DOCUMENT TYPES
FAILURE MODE ANALYSIS
FAILURES
FATIGUE
FRACTURE MECHANICS
FRACTURE PROPERTIES
FRACTURES
LINE DEFECTS
MATHEMATICAL MODELS
MATHEMATICS
MECHANICAL PROPERTIES
MECHANICS
MEETINGS
MICROSTRUCTURE
REVIEWS
SLIP
STATISTICS
STRESS ANALYSIS
SYSTEM FAILURE ANALYSIS
SYSTEMS ANALYSIS
VOIDS