Kinetics of O{sub 2} reduction on a Pt electrode covered with a thin film of solid polymer electrolyte
Journal Article
·
· Journal of the Electrochemical Society
- Case Western Reserve Univ., Cleveland, OH (United States)
The kinetics of O{sub 2} reduction on both oxidized and reduced Pt rotating disk surfaces covered with thin films (1 to 15 {micro}m) of recast polybenzimidazole (PBI) or Nafion have been examined in 0.1 M aqueous solutions of H{sub 3}PO{sub 4}, H{sub 2}SO{sub 4}, and HClO{sub 4} at 25.0 C. Polymer films were deposited on a Pt disk electrode by a spin-coating technique. Experiments were performed at different rotation rates and potential scan rates. This investigation was undertaken to establish to what extent the solid polymer electrolyte influences the mechanism and kinetics of O{sub 2} reduction. The number of electrons exchanged per O{sub 2} molecule and kinetic parameters for O{sub 2} reduction (reaction order with respect to O{sub 2}, Tafel slope/transfer coefficient, and exchange current density) are not changed in the presence of the polymer films, indicating that the reaction path and kinetics are not altered in the presence of recast PBI and Nafion films. The diffusion coefficient (D) and concentration (C) of O{sub 2} in recast films were determined by means of linear sweep voltammetry measurements in quiescent solution. The D and C values in polymer films immersed in acidic solutions were found to have different values than those in the solutions. D(O{sub 2}) is about 2.5 times lower in the recast films than in the solutions, whereas C(O{sub 2}) is slightly higher in the film. The largest concentration increase, by a factor of two, was found in PBI film in 0.1 M HClO{sub 4}. Cyclic voltammetric measurements under argon atmosphere have shown that PBI and Nafion recast films are electrochemically stable in the potential range between the onsets of H{sub 2} and O{sub 2} evolution. A decrease in the effective electrocatalyst surface area due to deposition of solid polymer films was 15 to 20%.
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 556812
- Journal Information:
- Journal of the Electrochemical Society, Journal Name: Journal of the Electrochemical Society Journal Issue: 9 Vol. 144; ISSN JESOAN; ISSN 0013-4651
- Country of Publication:
- United States
- Language:
- English
Similar Records
Oxygen reduction kinetics on a platinum RDE coated with a recast Nafion film
Journal Article
·
Mon Jun 01 00:00:00 EDT 1987
· J. Electrochem. Soc.; (United States)
·
OSTI ID:6290013