Simultaneous P and B diffusion, in-situ surface passivation, impurity filtering and gettering for high-efficiency silicon solar cells
- Georgia Inst. of Tech., Atlanta, GA (United States)
- Sandia National Labs., Albuquerque, NM (United States)
A technique is presented to simultaneously diffuse boron and phosphorus in silicon, and grow an in-situ passivating oxide in a single furnace step. It is shown that limited solid doping sources made from P and B Spin-On Dopant (SOD) films can produce optimal n{sup +} and p{sup +} profiles simultaneously without the deleterious effects of cross doping. A high quality passivating oxide is grown in-situ beneath the thin ({approximately} 60 {angstrom}) diffusion glass, resulting in low J{sub o} values below 100 fA/cm{sup 2} for transparent ({approximately} 100 {Omega}/{open_square}) phosphorus and boron diffusions. For the first time it is shown that impurities present in the boron SOD film can be effectively filtered out by employing separate source wafers, resulting in bulk lifetimes in excess of 1 ms for the sample wafers. The degree of lifetime degradation in the sources is related to the gettering efficiency of boron in silicon. This novel simultaneous diffusion, in-situ oxidation, impurity filtering and gettering technique was successfully used to produce 20.3% Fz, and 19.1% Cz solar cells, in one furnace step.
- Research Organization:
- Sandia National Labs., Albuquerque, NM (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 548685
- Report Number(s):
- SAND--97-2620C; CONF-970953--; ON: DE98001180; BR: YN0100000
- Country of Publication:
- United States
- Language:
- English
Similar Records
Utilization of Tabula Rasa to Stabilize Bulk Lifetimes in n-Cz Silicon for High-Performance Solar Cell Processing
Effect of oxidations on phosphorus-diffused crystalline-silicon substrates