On the requirement for a sharp notch or precrack to cause environmentally assisted crack initiation in {beta}-titanium alloys exposed to aqueous chloride environments
- Los Alamos National Lab., NM (United States)
- Univ. of Virginia, Charlottesville, VA (United States). Dept. of Materials Science and Engineering
The requirement of a sharp notch or precrack to cause environmental crack initiation of metastable {beta}-titanium alloys exposed to 0.6 M NaCl has been observed. The causal relationship has not been thoroughly examined, however. This paper seeks to explain the sharp notch requirement by examining notch acuity effects on a variety of parameters that affect HEAC susceptibility. These include the effects of a sharp notch on cation accumulation-hydrolysis-acidification, potential drop in solution and resulting hydrogen production, and localization of dynamic strain. It is shown that solution resistance down a sharp crack is two orders of magnitude larger for a fatigue precracked compact tension specimen than for a smooth bar. The potential drop down a sharp crack is severe enough to enable hydrogen production even when the applied potential is more positive than the reversible potential for hydrogen production. It`s also shown that a fatigue precrack results in an acidified crack tip chemistry (approximately pH 1) which is deleterious to HEAC resistance. The effects of a sharp notch on the interplay of mechanics, film rupture and hydrogen uptake are also examined. It is shown that the slip behavior at a sharp crack tip promotes localized film rupture and localized hydrogen uptake. Localization of hydrogen uptake may be critical for HEAC susceptibility in light of the large hydrogen concentration required to cause crack initiation (ca. 1,000 wt. ppm) and the lack of significant hydrogen uptake on filmed surfaces.
- Sponsoring Organization:
- Office of Naval Research, Washington, DC (United States)
- OSTI ID:
- 548513
- Report Number(s):
- CONF-960588-; ISBN 0-8031-2408-2; TRN: IM9750%%69
- Resource Relation:
- Conference: American Society for Testing and Materials (ASTM) symposium on effects of the environment and the initiation of crack growth, Orlando, FL (United States), 20-21 May 1996; Other Information: PBD: 1997; Related Information: Is Part Of Effects of the environment on the initiation of crack growth; Van Der Sluys, W.A.; Piascik, R.S.; Zawierucha, R. [eds.]; PB: [310] p.; ASTM special technical publication 1298
- Country of Publication:
- United States
- Language:
- English
Similar Records
Fracture Toughness Evaluation for Sandia Mock-up Stainless Steel Canister Weldment Using Spiral Notch Torsion Fracture Toughness Test
Corrosion fatigue crack growth behavior of a squeeze-cast Al-Si-Mg-Cu alloy with different precrack histories