The solidification behavior of Al-Mg alloys with Cu addition
Journal Article
·
· Scripta Metallurgica et Materialia; (United States)
- Inst. of Metal Research, Shenyang (China)
- Korea Inst. of Machinery and Metal, Changwon (Korea, Republic of)
Al-Mg alloys, as a lightweight auto-body material, have been subjected to intensive investigation. However, research on solidification behavior is limited. The binary Al-Mg alloy is a relatively simple alloy system. Its solidification processing is not complicated. But, the Al-Mg alloy equilibrium diagram shows that the eutectic temperature is very low. During solidification, elemental segregation will give rise to formation of a low melting point eutectic (LMPE). These LMPEs increase the difficulty in heat treatment processing, such as homogenization and annealing. High temperatures will lead to overheat and the LMPE remelting, while low temperatures will result in imperfect dissolution of the LMPE. All these factors give rise to reduction of mechanical properties. On the other hand, the addition of alloying elements and the presence of impure elements would make the solidification processing more complex. Some new LMPEs or insoluble constituents may be formed. But, these questions are far from being understood. It is the purpose of this study to investigate the solidification behavior and microstructure of Al-Mg alloys with the addition of Cu.
- OSTI ID:
- 5456109
- Journal Information:
- Scripta Metallurgica et Materialia; (United States), Journal Name: Scripta Metallurgica et Materialia; (United States) Vol. 30:4; ISSN 0956-716X; ISSN SCRMEX
- Country of Publication:
- United States
- Language:
- English
Similar Records
The solidification behavior of 8090 Al-Li alloy
Influence of the Composition on the Solidification Path, Microstructure Evolution and Mechanical Properties of Al-Cu-Mg Alloys
Microstructure and properties of additively manufactured Al–Ce–Mg alloys
Journal Article
·
Fri Oct 01 00:00:00 EDT 1993
· Metallurgical Transactions, B (Process Metallurgy); (United States)
·
OSTI ID:6085146
Influence of the Composition on the Solidification Path, Microstructure Evolution and Mechanical Properties of Al-Cu-Mg Alloys
Journal Article
·
Thu Nov 14 23:00:00 EST 2019
· Journal of Materials Engineering and Performance
·
OSTI ID:22970348
Microstructure and properties of additively manufactured Al–Ce–Mg alloys
Journal Article
·
Thu Mar 25 20:00:00 EDT 2021
· Scientific Reports
·
OSTI ID:1777746