Microtexture and grain boundary evolution during microstructural refinement processes in SUPRAL 2004
- Naval Postgraduate School, Monterey, CA (United States). Dept. of Mechanical Engineering
Electron backscatter pattern (EBSP) analysis of as-processed, processed and annealed, and superplastically deformed specimens of commercially processed SUPRAL 2004 material has been employed to reveal the boundary misorientation distribution and evolution. Earlier studies using X-ray diffraction (XRD) and transmission electron microscopy on this alloy have attributed the transition to microstructures capable of supporting extensive superplastic flow to continuous recrystallization occurring early in the deformation process. The micro- and mesotextural data of the present study show that the deformation texture evidence in the as-processed material persists without the formation of recrystallization texture components and remains up to the apparent onset of the grain boundary sliding (GBS) regime. Comparison of the correlated and uncorrelated boundary misorientation data illustrates that the development of boundary misoriented by {approximately}5 to 15 deg is not random in nature. There is no evidence of recrystallization involving the formation and migration of high-angle boundaries during the refinement process. Microtextural and boundary data from this study provide evidence that the microstructural transition enabling superplastic mechanical behavior of SUPRAL 2004 may be described by a recovery-dominated, continuous process involving the development of moderately misoriented boundaries and leading to a refined microstructure with a boundary distribution of low interfacial energy character.
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 544062
- Journal Information:
- Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science, Journal Name: Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science Journal Issue: 9 Vol. 28; ISSN 1073-5623; ISSN MMTAEB
- Country of Publication:
- United States
- Language:
- English
Similar Records
Grain structure and microtexture evolution during superplastic forming of a high strength Al-Zn-Mg-Cu alloy
Evolution of microstructure and microtexture during hot deformation in an advanced P/M nickel base superalloy