Heat treatment effects on tensile properties of V-(4-5) wt.% Cr-(4-5) wt.% Ti alloys
- Argonne National Lab., IL (United States)
Effects of thermomechanical treatments on microstructures and mechanical properties are of interest for long term application of V-Cr-Ti alloys in fusion reactor systems. Influence of thermal annealing at 1050{degrees}C on stress/strain behavior, maximum engineering strength, and uniform and total elongation were evaluated. The results show that multiple annealing has minimal effect on the tensile properties of V-(4-5)Cr-(4-5)Ti alloys tested at room temperature and at 500{degrees}C.
- Research Organization:
- Oak Ridge National Lab., TN (United States)
- DOE Contract Number:
- W-31109-ENG-38
- OSTI ID:
- 543200
- Report Number(s):
- DOE/ER--0313/22; ON: DE97008797
- Country of Publication:
- United States
- Language:
- English
Similar Records
Tensile properties of V-(4-5)Cr-(4-5)Ti alloys
Subtask 12D4: Baseline tensile properties of V-Cr-Ti alloys
Hardness recovery of 85% cold-worked V-Ti and V-Cr-Ti alloys upon annealing at 180{degrees}C to 1200{degrees}C
Technical Report
·
Sun Mar 31 23:00:00 EST 1996
·
OSTI ID:270417
Subtask 12D4: Baseline tensile properties of V-Cr-Ti alloys
Technical Report
·
Tue Feb 28 23:00:00 EST 1995
·
OSTI ID:415180
Hardness recovery of 85% cold-worked V-Ti and V-Cr-Ti alloys upon annealing at 180{degrees}C to 1200{degrees}C
Technical Report
·
Fri Mar 31 23:00:00 EST 1995
·
OSTI ID:115707