Swelling of Fe-Mn and Fe-Cr-Mn alloys at high neutron fluence
Technical Report
·
OSTI ID:5428598
Swelling data on neutron-irradiated simple Fe-Cr-Mn and Fe-Mn alloys, as well as commercial Fe-Cr-Mn base alloys are now becoming available at exposure levels approaching 50 dpa. The swelling rate decreases from the approx.1%/dpa found at lower exposures, probably due to the extensive formation of ferritic phases. As expected, commercial alloys swell less than the simple alloys.
- Research Organization:
- Hanford Engineering Development Lab., Richland, WA (USA)
- DOE Contract Number:
- AC06-76FF02170
- OSTI ID:
- 5428598
- Report Number(s):
- HEDL-7610; ON: DE86015490
- Country of Publication:
- United States
- Language:
- English
Similar Records
Phase development and swelling in Fe-Mn and Fe-Cr-Mn alloys during neutron irradiation
Swelling of Fe-Cr-Mn ternary alloys in FFTF
Neutron-induced swelling of Fe-Cr-Mn ternary alloys. [LMFBR]
Technical Report
·
Mon Mar 31 23:00:00 EST 1986
·
OSTI ID:6368963
Swelling of Fe-Cr-Mn ternary alloys in FFTF
Technical Report
·
Mon Oct 01 00:00:00 EDT 1984
·
OSTI ID:6215467
Neutron-induced swelling of Fe-Cr-Mn ternary alloys. [LMFBR]
Technical Report
·
Wed May 01 00:00:00 EDT 1985
·
OSTI ID:5746296