Effect of initial delamination on Mode 1 and Mode 2 interlaminar fracture toughness and fatigue fracture threshold
Static and fatigue double-cantilever beam (DCB) and end-notch flexure (ENF) tests were conducted to determine the effect of the simulated initial delamination in interlaminar fracture toughness, G(sub c), and fatigue fracture threshold, G(sub th). Unidirectional, 24-ply specimens of S2/SP250 glass/epoxy were tested using Kapton inserts of four different thickness - 13, 25, 75, and 130 microns, at the midplane at one end, or with tension or shear precracks, to simulate an initial delamination. To determine G(sub c), the fatigue fracture threshold below which no delamination growth would occur in less than 1 x 10(exp 6) cycles, fatigue tests were conducted by cyclically loading specimens until delamination growth was detected. Consistent values of model 1 fracture toughness, G(sub Ic), were measured from DCB specimens with inserts of thickness 75 microns or thinner, or with shear precracks. The fatigue DCB tests gave similar values of G(sub Ith) for the 13, 25, and 75 microns specimens. Results for the shear precracked specimens were significantly lower that for specimens without precracks. Results for both the static and fatigue ENF tests showed that measured G(IIc) and G(IIth) values decreased with decreasing insert thickness, so that no limiting thickness could be determined. Results for specimens with inserts of 75 microns or thicker were significantly higher than the results for precracked specimens or specimens with 13 or 25 microns inserts.
- Research Organization:
- National Aeronautics and Space Administration, Hampton, VA (United States). Langley Research Center
- OSTI ID:
- 5419001
- Report Number(s):
- N-91-26569; NASA-TM-104079; NAS-1.15:104079; AVSCOM-TR-91-B-005
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of stitching on impact and interlaminar properties of graphite/epoxy laminates
Mode I, Mode II, and mixed mode interlaminar fracture of woven fabric carbon/epoxy