Czochralski growth of single-crystal fayalite under controlled oxygen fugacity conditions. [Fe/sub 2/SiO/sub 4/]
- Oak Ridge National Lab., TN
Single-crystal boules of fayalite (Fe/sub 2/SiO/sub 4/) were grown in the temperature range 1165 to 1200/sup 0/C at 1 bar total pressure from high-purity oxide melts of 1.95:1 to 2.10:1 Fe:Si atom ratio. A modified Czochralski technique was used, with platinum crucibles inductively heated under oxygen fugacities, f(O/sub 2/), between 10/sup -9/ and 10/sup -12/ bar. The boules are up to 10 mm in diameter by 40 mm long and brownish-black in color. The best crystal homogeneity was obtained at growth rates of less than or equal to3 mm/hr from 2.1:1 Fe:Si melts at an f(O/sub 2/) of 10/sup -12/ bar at 1180 to 1185/sup 0/C. Colorimetric data indicate boule Fe/sup 3 +/ contents which increase with synthesis f(O/sub 2/) from 0.27% (10/sup -12/ bar) to 0.86% (10/sup -9/ bar). The typical orthorhombic unit-cell parameters are a = 4.8214 to 4.8219, b = 10.4774 to 10.4767, and c = 6.0880 to 6.0893 angstrom, varying slightly with synthesis f(O/sub 2/). The optical and infrared absorption spectrum is similar to that of natural fayalite, exhibiting a broad absorption band at 10,000 angstrom with transparency maxima at 7,000 and 25,000 angstrom. Samples appear stable up to melting at approx. 1202/sup 0/C(f(O/sub 2/) approx. = 10/sup -12/ bar), but lose weight and solidify incongruently.
- DOE Contract Number:
- W-7405-ENG-26
- OSTI ID:
- 5398888
- Journal Information:
- Am. Mineral.; (United States), Vol. 65
- Country of Publication:
- United States
- Language:
- English
Similar Records
Czochralski growth of single-crystal gehlenite (Ca/sub 2/Al/sub 2/SiO/sub 7/)
Local structural variation with oxygen fugacity in Fe2SiO4+x fayalitic iron silicate melts
Related Subjects
IRON SILICATES
CRYSTAL GROWTH
CRYSTAL STRUCTURE
CZOCHRALSKI METHOD
HIGH TEMPERATURE
IMPURITIES
LOW PRESSURE
CRYSTAL GROWTH METHODS
IRON COMPOUNDS
OXYGEN COMPOUNDS
SILICATES
SILICON COMPOUNDS
TRANSITION ELEMENT COMPOUNDS
360102* - Metals & Alloys- Structure & Phase Studies