Precision extrusion of hollow turbine vanes of oxide dispersion strengthened nickel chromium alloy by the filled billet method. Final report 13 March 1974--15 November 1975
Technical Report
·
OSTI ID:5379805
Precision extrusion of hollow vanes of oxide dispersion strengthened nickel chromium alloys was demonstrated on subscale specimens by using a modification of the filled billet method. The desired <100> microstructure was attained after heat treatment of extruded vanes. Stress rupture life at 2000 F at 11 ksi exceeded 100 hours. A full scale processing sequence based on subscale results is proposed.
- Research Organization:
- Polymet Corp., Cincinnati, Ohio (USA)
- DOE Contract Number:
- F33615-74-C-5069
- OSTI ID:
- 5379805
- Report Number(s):
- AD-A-041783
- Country of Publication:
- United States
- Language:
- English
Similar Records
Investigation of processing microstructures and properties of oxide dispersion strengthened cobalt alloy extruded shapes. Final technical report, 1 September 1974--31 December 1976. [Cu--20Ni--18Cr--4. 5Al--1. 75Y/sub 2/O/sub 3/]
Preparation and extrusion of multifilamentary NbTi conductor billets
PRODUCTION OF EXTRUSION BILLET OF HIGH TEMPERATURE AIRCRAFT ALLOYS BY POWDER METALLURGY. PHASE II. Second Interim Engineering Report for Period December 7, 1959-April 7, 1960
Technical Report
·
Fri Apr 01 00:00:00 EST 1977
·
OSTI ID:5379805
Preparation and extrusion of multifilamentary NbTi conductor billets
Conference
·
Wed Jan 01 00:00:00 EST 1975
·
OSTI ID:5379805
PRODUCTION OF EXTRUSION BILLET OF HIGH TEMPERATURE AIRCRAFT ALLOYS BY POWDER METALLURGY. PHASE II. Second Interim Engineering Report for Period December 7, 1959-April 7, 1960
Technical Report
·
Tue Oct 31 00:00:00 EST 1961
·
OSTI ID:5379805
Related Subjects
36 MATERIALS SCIENCE
TD-NICKEL CHROMIUM
EXTRUSION
RUPTURES
HEAT TREATMENTS
HIGH PRESSURE
SERVICE LIFE
TURBINE BLADES
VERY HIGH TEMPERATURE
ALLOYS
CERMETS
CHROMIUM ALLOYS
COMPOSITE MATERIALS
DISPERSIONS
FABRICATION
FAILURES
MATERIALS WORKING
NICKEL ALLOYS
360101* - Metals & Alloys- Preparation & Fabrication
360201 - Ceramics
Cermets
& Refractories- Preparation & Fabrication
360103 - Metals & Alloys- Mechanical Properties
360203 - Ceramics
Cermets
& Refractories- Mechanical Properties
TD-NICKEL CHROMIUM
EXTRUSION
RUPTURES
HEAT TREATMENTS
HIGH PRESSURE
SERVICE LIFE
TURBINE BLADES
VERY HIGH TEMPERATURE
ALLOYS
CERMETS
CHROMIUM ALLOYS
COMPOSITE MATERIALS
DISPERSIONS
FABRICATION
FAILURES
MATERIALS WORKING
NICKEL ALLOYS
360101* - Metals & Alloys- Preparation & Fabrication
360201 - Ceramics
Cermets
& Refractories- Preparation & Fabrication
360103 - Metals & Alloys- Mechanical Properties
360203 - Ceramics
Cermets
& Refractories- Mechanical Properties