Combined macroscopic and microscopic approach to the fracture of metals. Technical annual progress report, 1979-1980
The following results are reported: (1) extremely good theoretical-experimental correlation was found between our theoretical predictions based on asymptotic analysis with numerical finite element studies and the experimentally monitored crack growth for a large range of stable crack growth in 4140 steel; (2) a theoretical model was developed for the critical conditions of crack initiation at rigid particles as a precursor of ductile rupture in steels; (3) as part of environmentally sensitive fracture mechanisms, it was found that hydrogen can promote a ductile-to-brittle fracture transition with increasing charging current density in low carbon steel; and (4) a new variational principle has been established for the combined processes of plastic creep flow and grain boundary diffusion and has been constructively applied to the problem of cavity growth under creep conditions.
- Research Organization:
- Brown Univ., Providence, RI (USA). Div. of Engineering
- DOE Contract Number:
- AC02-80ER10556
- OSTI ID:
- 5347320
- Report Number(s):
- DOE/ER/10556-1; COO-3084-79
- Country of Publication:
- United States
- Language:
- English
Similar Records
Combined macroscopic and microscopic approach to the fracture of metals. Annual progress report, 1981-1982
Combined macroscopic and microscopic approach to the fracture of metals. Annual progress report, 1980-1981
Combined macroscopic and microscopic approach to the fracture of metals. Comprehensive progress report, 1979-1985
Technical Report
·
Thu Jul 01 00:00:00 EDT 1982
·
OSTI ID:5106792
Combined macroscopic and microscopic approach to the fracture of metals. Annual progress report, 1980-1981
Technical Report
·
Mon Jun 01 00:00:00 EDT 1981
·
OSTI ID:6458491
Combined macroscopic and microscopic approach to the fracture of metals. Comprehensive progress report, 1979-1985
Technical Report
·
Mon Jul 01 00:00:00 EDT 1985
·
OSTI ID:5111770