Effect of storage temperature of self-irradiation damage of /sup 238/Pu-substituted zirconolite
Journal Article
·
· Mater. Res. Soc. Symp. Proc.; (United States)
OSTI ID:5327683
/sup 238/Pu-substituted cubic zirconolite (CaPuTi/sub 2/O/sub 7/) was stored at ambient temperature, 575 K and 875 K until alpha decay doses of 2.4 to 3.6 x 10/sup 25//m/sup 3/ had been accumulated. The ambient temperature material swelled to a saturation value of 5.5 vol%, and the originally crystalline structure was transformed to one with an amorphous matrix and small domains that had retained their crystallinity. At 575 K lesser amounts of swelling (4.1 vol%) and transformation were observed, reflecting concurrent partial recovery. The material held at 875 K remained crystalline, swelled only 0.4 vol%, and exhibited formation of isolated defect clusters.
- Research Organization:
- Los Alamos National Lab., NM
- OSTI ID:
- 5327683
- Journal Information:
- Mater. Res. Soc. Symp. Proc.; (United States), Vol. 15
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of storage temperature on self-irradiation damage of /sup 238/Pu-substituted zirconolite
Structural change in /sup 238/Pu-substituted zirconolite on recovery from the metamict state
Preparation and Characterization of {sup 238}Pu-Ceramics for Radiation Damage Experiments
Conference
·
Fri Jan 01 00:00:00 EST 1982
·
OSTI ID:5327683
+2 more
Structural change in /sup 238/Pu-substituted zirconolite on recovery from the metamict state
Conference
·
Wed Jan 01 00:00:00 EST 1986
· Mater. Res. Soc. Symp. Proc.; (United States)
·
OSTI ID:5327683
+1 more
Preparation and Characterization of {sup 238}Pu-Ceramics for Radiation Damage Experiments
Technical Report
·
Thu Jun 15 00:00:00 EDT 2000
·
OSTI ID:5327683
+3 more
Related Subjects
36 MATERIALS SCIENCE
12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE WASTES FROM NUCLEAR FACILITIES
ZIRCONOLITE
SELF-IRRADIATION
ALPHA DECAY
EXPERIMENTAL DATA
HIGH-LEVEL RADIOACTIVE WASTES
PHYSICAL RADIATION EFFECTS
PLUTONIUM 238
RADIOACTIVE WASTE DISPOSAL
STABILITY
TEMPERATURE EFFECTS
ACTINIDE COMPOUNDS
ACTINIDE ISOTOPES
ACTINIDE NUCLEI
ALKALINE EARTH METAL COMPOUNDS
ALPHA DECAY RADIOISOTOPES
CALCIUM COMPOUNDS
CALCIUM OXIDES
CHALCOGENIDES
DATA
DECAY
EVEN-EVEN NUCLEI
HEAVY NUCLEI
INFORMATION
IRON COMPOUNDS
IRON OXIDES
IRRADIATION
ISOTOPES
MANAGEMENT
MATERIALS
MINERALS
NUCLEI
NUMERICAL DATA
OXIDE MINERALS
OXIDES
OXYGEN COMPOUNDS
PLUTONIUM ISOTOPES
RADIATION EFFECTS
RADIOACTIVE MATERIALS
RADIOACTIVE WASTES
RADIOISOTOPES
THORIUM COMPOUNDS
THORIUM OXIDES
TITANIUM COMPOUNDS
TITANIUM OXIDES
TRANSITION ELEMENT COMPOUNDS
WASTE DISPOSAL
WASTE MANAGEMENT
WASTES
YEARS LIVING RADIOISOTOPES
ZIRCONIUM COMPOUNDS
ZIRCONIUM OXIDES
360605* - Materials- Radiation Effects
052002 - Nuclear Fuels- Waste Disposal & Storage
12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE WASTES FROM NUCLEAR FACILITIES
ZIRCONOLITE
SELF-IRRADIATION
ALPHA DECAY
EXPERIMENTAL DATA
HIGH-LEVEL RADIOACTIVE WASTES
PHYSICAL RADIATION EFFECTS
PLUTONIUM 238
RADIOACTIVE WASTE DISPOSAL
STABILITY
TEMPERATURE EFFECTS
ACTINIDE COMPOUNDS
ACTINIDE ISOTOPES
ACTINIDE NUCLEI
ALKALINE EARTH METAL COMPOUNDS
ALPHA DECAY RADIOISOTOPES
CALCIUM COMPOUNDS
CALCIUM OXIDES
CHALCOGENIDES
DATA
DECAY
EVEN-EVEN NUCLEI
HEAVY NUCLEI
INFORMATION
IRON COMPOUNDS
IRON OXIDES
IRRADIATION
ISOTOPES
MANAGEMENT
MATERIALS
MINERALS
NUCLEI
NUMERICAL DATA
OXIDE MINERALS
OXIDES
OXYGEN COMPOUNDS
PLUTONIUM ISOTOPES
RADIATION EFFECTS
RADIOACTIVE MATERIALS
RADIOACTIVE WASTES
RADIOISOTOPES
THORIUM COMPOUNDS
THORIUM OXIDES
TITANIUM COMPOUNDS
TITANIUM OXIDES
TRANSITION ELEMENT COMPOUNDS
WASTE DISPOSAL
WASTE MANAGEMENT
WASTES
YEARS LIVING RADIOISOTOPES
ZIRCONIUM COMPOUNDS
ZIRCONIUM OXIDES
360605* - Materials- Radiation Effects
052002 - Nuclear Fuels- Waste Disposal & Storage