Americium/Curium Vitrification Process Development
The successful demonstration of sequentially drying, calcining and vitrifying an oxalate slurry in the Drain Tube Test Stand (DTTS) vessel provided the process basis for testing on a larger scale in a cylindrical induction heated melter. A single processing issue, that of batch volume expansion, was encountered during the initial stages of testing. The increase in batch volume centered on a sintered frit cap and high temperature bubble formation. The formation of a sintered frit cap expansion was eliminated with the use of cullet. Volume expansions due to high temperature bubble formation (oxygen liberation from cerium reduction) were mitigated in the DTTS melter vessel through a vessel temperature profile that effectively separated the softening point of the glass cullet and the evolving oxygen from cerium reduction. An increased processing temperature of 1470 degrees C and a two hour hold time to fine any remaining bubbles successfully reduced bubbles in the poured glass to an acceptable level. The success of the preliminary process demonstrations provided a workable process basis that was directly applicable to the newly installed Cylindrical Induction Melter (CIM) system, making the batch flowsheet the preferred option for vitrification of the americium-curium surrogate feed stream.
- Research Organization:
- Savannah River Site
- Sponsoring Organization:
- DOE
- DOE Contract Number:
- AC09-96SR18500
- OSTI ID:
- 5299
- Report Number(s):
- WSRC-MS-98-00864, Rev. 1; ON: DE00005299
- Country of Publication:
- United States
- Language:
- English
Chemistry of Rare Earth Oxalate Vitrification
|
journal | January 1999 |
Similar Records
Bed expansion crucible tests
Development of the Am/Cm Batch Vitrification Process