Epitaxial YBa[sub 2]Cu[sub 3]O[sub 7[minus][delta]] thin films on SrRuO[sub 3]/Pt/MgO
- Superconductivity Technology Center, Los Alamos National Laboratory, Los Alamos, New Mexico 87545 (United States)
Epitaxial YBa[sub 2]Cu[sub 3]O[sub 7[minus][delta]] (YBCO) thin films were deposited on (100) MgO using platinum and SrRuO[sub 3] (SRO) buffer layers by pulsed laser deposition. The films were (001) textured normal to substrate surface with a high degree of in-plane orientation with respect to the substrate's major axes. YBCO films showed superconducting transition temperature ([ital T][sub co]) at 91 K and critical current densities were found to be 2--3[times]10[sup 6] A/cm[sup 2] at 77 K and zero field. An ion beam minimum channeling yield of 16% was obtained for YBCO films, indicating high crystallinity. The orientation relationship for this epitaxial multilayer structure was found to be (100) YBCO[parallel](100) SRO[parallel](100)Pt[parallel](100) MgO. This result showed that high-quality superconducting thin films can be deposited on metal with an appropriate buffer layer.
- OSTI ID:
- 5291768
- Journal Information:
- Applied Physics Letters; (United States), Vol. 64:5; ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- English
Similar Records
Growth and Superconducting Properties of YBa2Cu3O 7-d Films on Conductive SrRuO3 and LaNiO3 Multilayers for
Growth and superconducting properties of YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} films on conductive SrRuO{sub 3} and LaNiO{sub 3} multilayers for coated conductor applications
Related Subjects
BARIUM OXIDES
EPITAXY
COPPER OXIDES
CUPRATES
HIGH-TC SUPERCONDUCTORS
YTTRIUM OXIDES
ABLATION
BUFFERS
CRITICAL CURRENT
CRYSTAL STRUCTURE
LASER RADIATION
MORPHOLOGY
TRANSITION TEMPERATURE
ALKALINE EARTH METAL COMPOUNDS
BARIUM COMPOUNDS
CHALCOGENIDES
COPPER COMPOUNDS
CURRENTS
ELECTRIC CURRENTS
ELECTROMAGNETIC RADIATION
OXIDES
OXYGEN COMPOUNDS
PHYSICAL PROPERTIES
RADIATIONS
SUPERCONDUCTORS
THERMODYNAMIC PROPERTIES
TRANSITION ELEMENT COMPOUNDS
YTTRIUM COMPOUNDS
360207* - Ceramics
Cermets
& Refractories- Superconducting Properties- (1992-)
360201 - Ceramics
Cermets
& Refractories- Preparation & Fabrication