Laser photodecomposition of sintered YBa sub 2 Cu sub 3 O sub 6+ x : Ejected species population distributions and initial kinetic energies for the laser ablation wavelengths 351, 248, and 193 nm
- Laser Chemistry Spectroscopy Department, Aerophysics Laboratory, The Aerophysics Corporation, P.O. Box 92957, Los Angeles, California (USA)
We present experimental results of photoablated product and kinetic energy (KE) distributions from the ultraviolet laser ablation of a sintered YBa{sub 2}Cu{sub 3}O{sub 6+{ital x}} wafer at the laser wavelengths 351, 248, and 193 nm. Data is presented which spans the laser fluence range beginning at the threshold for species ejection (50 mJ/cm{sup 2}) to nearly that required for the formation of an above surface plasma (800 mJ/cm{sup 2}). The goal of this experiment was to measure changes in the photophysical process as the incident laser fluence was increased above the threshold value. Our results show, that near the laser threshold fluence, the photoejected products consist of small atomic and oxide species. An unforeseen result for the UV laser wavelengths used, is the lack of CuO{sup +}/CuO and free oxygen (O{sup +}/O, O{sup +}{sub 2}/O{sub 2}) in the mass spectrum. In addition, the product distributions are {ital dependent} on the laser wavelength. Measured also, at laser threshold fluence, are the nascent photoejected cation kinetic energy distribution. Here our results show that the KE distribution is independent of both the laser fluence and the wavelength. The mean kinetic energy, {l angle}KE{r angle}, exceeds 3 eV and cannot be explained by a thermal excitation process. With increasing laser fluence (50% above threshold), we detected the photodissociation of the ejected oxide species, and the appearance of the O{sup {minus}} anion. Unlike the KE of the cation species, the O{sup {minus}} kinetic energy is nearly thermal ({lt}1 eV). With additional increases in the laser fluence, we measure the photoejection of slow KE neutral species and the simultaneous KE enhancement of the laser ablated ions (KE{gt}30 eV). At the highest laser fluences used in this experiment, it was noted that atomic cluster formations were enhanced. These compounds are presumably formed in the expanding ablated plume.
- OSTI ID:
- 5172309
- Journal Information:
- Journal of Applied Physics; (United States), Vol. 70:8; ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Laser induced effects on ZnO targets upon ablation at 266 and 308 nm wavelengths
Internal state populations and velocity distributions of monatomic species ejected after the 1064 nm laser irradiation of barium
Related Subjects
BARIUM OXIDES
ABLATION
COPPER OXIDES
YTTRIUM OXIDES
MASS SPECTRA
THRESHOLD ENERGY
ULTRAVIOLET RADIATION
ALKALINE EARTH METAL COMPOUNDS
BARIUM COMPOUNDS
CHALCOGENIDES
COPPER COMPOUNDS
ELECTROMAGNETIC RADIATION
ENERGY
OXIDES
OXYGEN COMPOUNDS
RADIATIONS
SPECTRA
TRANSITION ELEMENT COMPOUNDS
YTTRIUM COMPOUNDS
360204* - Ceramics
Cermets
& Refractories- Physical Properties