Fabrication of zircon for disposition of weapons plutonium
- and others
This is the final report of a one-year, Laboratory-Directed Research and Development (LDRD) project at the Los Alamos National Laboratory (LANL). In an effort to address the problems of long term storage and nuclear waste minimization, zircon has been proposed as a host medium for plutonium and other actinides recovered from dismantled nuclear weapons. The objective of this work is to investigate the feasibility of large scale fabrication of Pu-bearing zircon. Since PuO{sub 2} is thermodynamically less stable than ZrO{sub 2}, it is expected that the process parameters determined for synthesizing ZrSiO{sub 4} (zircon) would be applicable to those for PuSiO{sub 4} (Pu-zircon). Furthermore, since the foremost concern in plutonium processing is the potential for contamination release, this work emphasizes the development of process parameters, using zircon first, to anticipate potential material problems in the containment system for reaction mixtures during processing. Stoichiometric mixtures of ZrO{sub 2} and SiO{sub 2}, in hundred-gram batches, have been subjected to hot isostatic pressing (HIP) at temperatures near 1,500 C and pressures approximately 10,000 psi. The product materials have been analyzed by x-ray powder diffraction, and are found to consist of zircon after approximately two hours of reaction time. From this work, it is clear that the fabrication of large quantities of Pu-zircon is feasible. The most notable result of this work is evidence for the existence of container problems. This result, in turn, suggests potential solutions to these problems. Experiments with the quartz inner container, the glass sealant, a sacrificial metal barrier, and a metal outer container are being investigated to mitigate these potential hazards.
- Research Organization:
- Los Alamos National Lab. (LANL), Los Alamos, NM (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- W-7405-ENG-36
- OSTI ID:
- 515554
- Report Number(s):
- LA-UR-97-1519; ON: DE97007839; TRN: 97:016075
- Resource Relation:
- Other Information: PBD: [1997]
- Country of Publication:
- United States
- Language:
- English
Similar Records
Thermodynamics of CeSiO4: Implications for Actinide Orthosilicates
Microstructure of the simulated Idaho Chemical Processing Plant (ICPP) nuclear wastes and the effect of radiation damage