Crack initiation and crack growth behavior of carbon and low-alloy steels
- Argonne National Lab., IL (United States). Energy Technology Div.
Section III of the ASME Boiler and Pressure Vessel Code specifies fatigue design curves for structural materials. These curves were based on tests of smooth polished specimens at room temperature in air. The effects of reactor coolant environments are not explicitly addressed by the Code design curves, but recent test data illustrate potentially significant effects of LWR coolant environments on the fatigue resistance of carbon and low-alloy steels. Under certain loading and environmental conditions, fatigue lives of test specimens may be a factor of {approx}70 shorter than in air. Results of fatigue tests that examine the influence of reactor environment on crack imitation and crack growth of carbon and low-alloy steels are presented. Crack lengths as a function of fatigue cycles were determined in air by a surface replication technique, and in water by block loading that leaves marks on the fracture surface. Decreases in fatigue life of low-alloy steels in high-dissolved-oxygen (DO) water are primarily caused by the effects of environment during early stages of fatigue damage, i.e., growth of short cracks <100 {micro}m in depth. For crack sizes of >100 {micro}m, crack growth rates in high-DO water are higher than in air by one order of magnitude. The effects of LWR environments on growth of short cracks are discussed.
- Research Organization:
- Argonne National Lab., IL (United States)
- Sponsoring Organization:
- Nuclear Regulatory Commission, Washington, DC (United States)
- DOE Contract Number:
- W-31109-ENG-38
- OSTI ID:
- 505296
- Report Number(s):
- ANL/ET/CP--91269; CONF-970726--18; ON: DE97007114
- Country of Publication:
- United States
- Language:
- English
Similar Records
Fatigue crack initiation in carbon and low-alloy steels in light water reactor environments : mechanism and prediction.
Overview of fatigue crack initiation in carbon and low-alloy steels in light water reactor environments
Crack initiation in smooth fatigue specimens of austenitic stainless steel in light water reactor environments.
Conference
·
Mon Jan 26 23:00:00 EST 1998
·
OSTI ID:8874
Overview of fatigue crack initiation in carbon and low-alloy steels in light water reactor environments
Journal Article
·
Sun Jan 31 23:00:00 EST 1999
· Journal of Pressure Vessel Technology
·
OSTI ID:328399
Crack initiation in smooth fatigue specimens of austenitic stainless steel in light water reactor environments.
Conference
·
Thu Apr 08 00:00:00 EDT 1999
·
OSTI ID:12388