Corrosion phenomena on alloy 625 in aqueous solutions containing hydrochloric acid and oxygen under subcritical and supercritical conditions
- Forschungszentrum Karlsruhe (Germany)
Supercritical Water Oxidation (SCWO) is a very effective process to destroy hazardous aqueous wastes containing organic contaminants. The main target applications in the USA are the destruction of DOD and DOE wastes such as rocket fuels and explosives, warfare agents and organics present in low level radioactive liquid wastes. Alloy 625 is frequently used as reactor material for Supercritical Water Oxidation (SCWO) applications. This is due to the favorable combination of mechanical properties, corrosion resistance, price and availability. Nevertheless, the corrosion of alloy 625 like the corrosion of other Ni-base alloys during oxidation of hazardous organic waste containing chloride proceeds too fast and is a major problem in SCWO applications. In these experiments high pressure, high-temperature resistant tube reactors made of alloy 625 were used as specimens. They were exposed to SCWO conditions, without organics, at temperatures up to 500 C and pressures up to 37 MPa for up to 150 h. Simultaneously, coupons also made from alloy 625 are exposed inside the test tubes. The most important corrosion problem for alloy 625 is pitting and intercrystalline corrosion at temperatures near the critical temperature, i.e. in the preheater and cooling sections of the test tubes. Under certain conditions, stress corrosion cracking appears and leads to premature failure of the test reactors. The corrosion products were insoluble in supercritical water and formed thick layers in the supercritical part of the reactor. Under these layers only minor corrosion occurred. 33 refs.
- OSTI ID:
- 504734
- Report Number(s):
- CONF-970332-; TRN: 97:013473
- Resource Relation:
- Conference: Corrosion 97. 52. annual corrosion conference of the National Association of Corrosion Engineers: economics and performance - bridging the gap and NACExpo, New Orleans, LA (United States), 9-14 Mar 1997; Other Information: PBD: 1997; Related Information: Is Part Of Corrosion/97 conference papers; PB: [4584] p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Corrosion screening tests with Ni-base alloys in supercritical water containing hydrochloric acid and oxygen
Evaluation of materials performance in a supercritical wet oxidation system