Magnetic properties of Y(Fe{sub 0.8}M{sub 0.2}){sub 11.3}Nb{sub 0.7} compounds with M=Mn, Fe, Co, Ni, Al, and Ga
- State Key Laboratory of Magnetism, Institute of Physics, Chinese Academy of Sciences, P.O. Box 603, Beijing 10080, Peoples Republic of (China)
- Van der Waals-Zeeman Institute, University of Amsterdam, Valckenierstraat 65, 1018 XE Amsterdam (The Netherlands)
Structural and magnetic properties of Y(Fe{sub 0.8}M{sub 0.2}){sub 11.3}Nb{sub 0.7} compounds with M=Mn, Fe, Co, Ni, Al, and Ga have been investigated. The x-ray diffraction patterns of aligned samples show that, for M=Mn, Fe, Co, Ni, the compounds exhibit easy axis anisotropy while for M=Al and Ga the compounds have planar anisotropy. The anisotropy fields of Y(Fe{sub 0.8}Mn{sub 0.2}){sub 11.3}Nb{sub 0.7} increase monotonously with decreasing temperature. The influence on the Curie temperature and the magnetization due to the various substitutional atoms are discussed. {copyright} {ital 1997 American Institute of Physics.}
- OSTI ID:
- 496561
- Report Number(s):
- CONF-961141-; ISSN 0021-8979; TRN: 97:016253
- Journal Information:
- Journal of Applied Physics, Vol. 81, Issue 8; Conference: 41. annual conference on magnetism and magnetic materials, Atlanta, GA (United States), 12-15 Nov 1996; Other Information: PBD: Apr 1997
- Country of Publication:
- United States
- Language:
- English
Similar Records
Isotropic nanocrystalline Sm(Fe,Co)11.3Ti0.7 magnets modified with B and Zr
Chemical compatibility of (La{sub 0.6}Ca{sub 0.4}){sub x}Fe{sub 0.8}M{sub 0.2}O{sub 3} (x = 1, 0.9; M = Cr, Mn, Co, Ni) with YSZ
Chemical compatibility of (La{sub 0.6}Ca{sub 0.4}){sub x}Fe{sub 0.8}M{sub 0.2}O{sub 3} with yttria-stabilized zirconia
Journal Article
·
Tue Mar 02 00:00:00 EST 2021
· Journal of Magnetism and Magnetic Materials
·
OSTI ID:496561
Chemical compatibility of (La{sub 0.6}Ca{sub 0.4}){sub x}Fe{sub 0.8}M{sub 0.2}O{sub 3} (x = 1, 0.9; M = Cr, Mn, Co, Ni) with YSZ
Book
·
Sun Dec 31 00:00:00 EST 1995
·
OSTI ID:496561
+1 more
Chemical compatibility of (La{sub 0.6}Ca{sub 0.4}){sub x}Fe{sub 0.8}M{sub 0.2}O{sub 3} with yttria-stabilized zirconia
Journal Article
·
Sat Feb 01 00:00:00 EST 1997
· Journal of the Electrochemical Society
·
OSTI ID:496561
+3 more