The rare earth silicon phosphides LnSi{sub 2}P{sub 6} (Ln = La, Ce, Pr, and Nd)
- Universitaet Muenster (Germany)
The title compounds were prepared in well-crystallized form from a tin flux and their crystal structure was determined from single-crystal diffractometer data of LaSi{sub 2}P{sub 6}: Cmc2{sub 1}, a = 1012.9(3) pm, b = 2817.5(7) pm, c = 1037.4(5) pm, Z = 16, R = 0.034 for 3303 structure factors and 181 variable parameters. The structure of the isotypic compound CeSi{sub 2}P{sub 6} was also refined from single-crystal X-ray data: a = 1011.8(4) pm, b = 2803.1(8) pm, c = 1031.1(4) pm, R = 0.035 for 2132 F values and 181 variables. The silicon and the phosphorus atoms could be distinguished by comparing their occupancy parameters obtained from both structure refinements. The assignments agree with those deduced by structure-chemical arguments. These atoms form a three-dimensionally infinite framework polyanion, which accommodates four different kinds of rare earth atoms: three with nine and one with ten phosphorus neighbors. The silicon atoms are all in tetrahedral phosphorus coordination. There are phosphorus atoms which have only two rare earth and two silicon neighbors, but most phosphorus atoms have--in addition to the rare earth and silicon atoms--phosphorus neighbors, thus forming P{sub 3}, P{sub 4}, P{sub 5}, and P{sub 6} units. Using oxidation numbers, the compounds can be rationalized with the formulas Ln{sup 3+}(Si{sub 2}P{sub 6}){sub 3-} and Ln{sup 3+}(Si{sup 4+}){sub 2}(P{sub 6}){sup 11-}, where the octet rule is obeyed for the silicon and phosphorus atoms and two electrons are counted for each Si-P and P-P interaction.
- OSTI ID:
- 494456
- Journal Information:
- Journal of Solid State Chemistry, Vol. 124, Issue 2; Other Information: PBD: Jul 1996
- Country of Publication:
- United States
- Language:
- English
Similar Records
Preparation and crystal structures of the rare earth nitrido-oxosilicates and nitridosilicates with the general formula R{sub 6+x/3}Si{sub 11}N{sub 20+x}O{sub 1-x} and the ideal compositions R{sub 6}Si{sub 11}N{sub 20}O and R{sub 6.33}Si{sub 11}N{sub 21}, respectively (R=Y and Gd-Lu)
Third time's the charm: intricate non-centrosymmetric polymorphism in Ln SiP 3 ( Ln = La and Ce) induced by distortions of phosphorus square layers