EXPERIMENTAL APPROXIMATION OF MELTING TEMPERATURES FOR VARIOUS ALLOYS OF Ni- Ti-Cr-Mo-W-Nb SYSTEM (in Russian)
Journal Article
·
· Zhur. Neorg. Khim.
OSTI ID:4840111
Approximate fusing diagrams of Ni and Ti enriched hexacomponent Ni-- Ti-- Cr -- Mo-- W-- Nb alloys were constructed on the basis of published data for binary and ternary alloys. The approximate melting temperature for 65% Ni-15% Cr- 5% Mo--5% Ti-7% W-3% Nb was found at 1360 deg C and for 70% Ni-10% Cr-5% Mo-5% Ti- 7% W-3% Nb at 1376 deg C, experimentally verified melting tcmperatures were 1356 deg and 1350 deg C, respectively. (R.Y.J.)
- Research Organization:
- Originating Research Org. not identified
- NSA Number:
- NSA-16-019411
- OSTI ID:
- 4840111
- Journal Information:
- Zhur. Neorg. Khim., Journal Name: Zhur. Neorg. Khim. Vol. Vol: 7
- Country of Publication:
- Country unknown/Code not available
- Language:
- Russian
Similar Records
STAINLESS Cr-Mn-Ni STEEL WITH Ti, Nb, AND Mo
THE CORROSION BEHAVIOR OF THE NICKEL-CHROMIUM ALLOY INCONEL AND INCONEL AND NIOBIUM ALLOYS IN A PRESSURIZED WATER REACTOR. PART II
THE INFLUENCE OF THE TIME FACTOR ON THE COMPOSITION-HEAT RESISTANCE DIAGRAM OF FIVE-COMPONENT Ni-Cr-W-Ti-Al ALLOYS
Journal Article
·
Wed Jan 31 23:00:00 EST 1962
· Metalloved. i Termichesk. Obrabotka Metal.
·
OSTI ID:4799823
THE CORROSION BEHAVIOR OF THE NICKEL-CHROMIUM ALLOY INCONEL AND INCONEL AND NIOBIUM ALLOYS IN A PRESSURIZED WATER REACTOR. PART II
Journal Article
·
Tue May 01 00:00:00 EDT 1962
· Energie nucleaire
·
OSTI ID:4792235
THE INFLUENCE OF THE TIME FACTOR ON THE COMPOSITION-HEAT RESISTANCE DIAGRAM OF FIVE-COMPONENT Ni-Cr-W-Ti-Al ALLOYS
Journal Article
·
Sat Jun 11 00:00:00 EDT 1960
· Doklady Akad. Nauk S.S.S.R.
·
OSTI ID:4160597