INHIBITION OF STRESS-CORROSION CRACKING OF AUSTENITIC STAINLESS STEEL
Journal Article
·
· Nuclear Eng.
OSTI ID:4837619
The effects of a number of inhibitors on the stresscorrosion behavior of an 18/9 Cr-Ni, Nb stabilized, austenitic stainless steel were investigated in tests closely simulating severe conditions likely to be inet in practice. In chloride environinents tri-sodium phosphate present in a ratio of not less than 1: 2, tri-sodium phosphate: sodium chloride, was shown to prevent, or at least greater delay, stress-corrosion cracking. its use in conjunction with other currently accepted inethods of protection would significantly reduce the risk of attack under actual operating conditions. (auth)
- Research Organization:
- Brown-Firth Research Labs., Sheffield, Eng.
- NSA Number:
- NSA-15-032496
- OSTI ID:
- 4837619
- Journal Information:
- Nuclear Eng., Journal Name: Nuclear Eng. Vol. Vol: 6
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
Effect of halogens and inhibitors on the external stress corrosion cracking of Type 304 austenitic stainless steel
Effects of fluoride and other halogen ions on the external stress corrosion cracking of Type 304 austenitic stainless steel
MECHANISM OF STRESS CORROSION OF AUSTENITIC STAINLESS STEELS IN HIGH- TEMPERATURE CHLORIDE WATERS. Technical Report No. 2
Conference
·
Fri Oct 31 23:00:00 EST 1997
·
OSTI ID:543469
Effects of fluoride and other halogen ions on the external stress corrosion cracking of Type 304 austenitic stainless steel
Technical Report
·
Tue Jul 01 00:00:00 EDT 1997
·
OSTI ID:505259
MECHANISM OF STRESS CORROSION OF AUSTENITIC STAINLESS STEELS IN HIGH- TEMPERATURE CHLORIDE WATERS. Technical Report No. 2
Technical Report
·
Mon Mar 31 23:00:00 EST 1958
·
OSTI ID:4321333