ORIENTATION OF CAST BERYLLIUM
Journal Article
·
· Trans. Met. Soc. AIME
OSTI ID:4836758
The texture method (utilizing monochromatic copper radiation) was applied to determine the orientation of the columnar grains of two vacuum-cast Be ingots 3 in. in diameter. The Debye pattern was compared with theoretical patterns for various orientations. No significant preference for the direction of columnar growth is indicated. It is considered that the lack of a preferred orientation is because of the occurrence of the phase transformation which masked the original solidification orientation. (L.T.W.)
- Research Organization:
- Illinois Inst. of Tech., Chicago
- NSA Number:
- NSA-15-029766
- OSTI ID:
- 4836758
- Journal Information:
- Trans. Met. Soc. AIME, Journal Name: Trans. Met. Soc. AIME Vol. Vol: 221
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
BERYLLIUM RESEARCH FOR DEVELOPMENT IN THE AREA OF CASTING. Period covered June 15, 1958 to October 14, 1959
Crystallographic orientation of columnar grains in cast beryllium
Effect of shape variations on the structure and crystallography of directionally solidified {gamma}/{gamma}{prime}-{alpha} eutectic composites
Technical Report
·
Fri Jul 31 00:00:00 EDT 1959
·
OSTI ID:4186425
Crystallographic orientation of columnar grains in cast beryllium
Journal Article
·
Thu Mar 31 23:00:00 EST 1977
· Metallography; (United States)
·
OSTI ID:5257467
Effect of shape variations on the structure and crystallography of directionally solidified {gamma}/{gamma}{prime}-{alpha} eutectic composites
Journal Article
·
Tue Aug 01 00:00:00 EDT 1995
· Scripta Metallurgica et Materialia
·
OSTI ID:103591