HIGH TEMPERATURE MATERIALS PROGRAM. Progress Report No. 4, Part A, August 1, 1961-September 30, 1961
Technical Report
·
OSTI ID:4833174
Samples of two compositions of BeO plus MgO were placed in the Engineering Test Reactor. Designs for cartridges to be used in 600 and 1000 deg C irradiations were completed. Sintering conditions were established for preparing rods of the remaining our of the six BeO compositions to be tested. A more precise method of measuring grain size was adopted. Physical property measurements consisted largely of non-destructive tests on both control and irradiation specimens. (M.C.G.)
- Research Organization:
- General Electric Co. Flight Propulsion Lab. Dept., Cincinnati
- DOE Contract Number:
- AT(40-1)-2847
- NSA Number:
- NSA-16-002176
- OSTI ID:
- 4833174
- Report Number(s):
- GEMP-4A
- Resource Relation:
- Other Information: Orig. Receipt Date: 31-DEC-62
- Country of Publication:
- United States
- Language:
- English
Similar Records
HIGH-TEMPERATURE MATERIALS PROGRAM. Progress Report No. 12, Part A
HIGH-TEMPERATURE MATERIALS PROGRAM PROGRESS REPORT NO. 22, PART A
SUMMARY OF HIGH TEMPERATURE MATERIALS WORK PERFORMED IN FY 61, PART A, MAY 1, 1961-JUNE 30, 1961
Technical Report
·
Fri Jun 15 00:00:00 EDT 1962
·
OSTI ID:4833174
HIGH-TEMPERATURE MATERIALS PROGRAM PROGRESS REPORT NO. 22, PART A
Technical Report
·
Tue Apr 30 00:00:00 EDT 1963
·
OSTI ID:4833174
SUMMARY OF HIGH TEMPERATURE MATERIALS WORK PERFORMED IN FY 61, PART A, MAY 1, 1961-JUNE 30, 1961
Technical Report
·
Fri Dec 01 00:00:00 EST 1961
·
OSTI ID:4833174